Photoluminescence (PL), electron spin resonance (ESR), and high resolution transmission electron microscopy (HRTEM) were used to investigate the luminescence mechanism in Si nanocrystals. Si ions were implanted in SiO2 films at 190 keV to a dose of 3×1017/cm2.An intense photoluminescence (PL) band at 755 nm (1.65 eV) was observed when the implanted films were annealed above 800 °C in air or in nitrogen. HRTEM images showed Si nanocrystals of sizes between 1 and 6 nm from these annealed samples. ESR indicated Si dangling bonds. Upon annealing at 900 °C in air a few times, the particle sizes were reduced to less than 2 nm due to oxidation. The red PL band is attributed to emission from Si nanocrystals.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.