Introduction: Enamel etching is an important and necessary phase of bonding protocol. Different etching duration and different acid concentration can be used to prepare the tooth surface for bonding. Generally, the longer the etching duration and the higher the acid concentration, the stronger the bond strength between bracket and tooth surface. However recent studies are focused on lowering the etch concentration during bonding of brackets. Aim of the study: To evaluate the enamel damage caused by different acid concentrations during enamel etching; to determine the impact of acid concentration during enamel etching on the bond strength of orthodontic brackets; to determine the etch concentration which will achieve the optimal bond strength while minimizing enamel damage. Material and methods: The material for our In Vitro study consisted of 30 intact premolar teeth, extracted for orthodontic reasons. The teeth were categorized in three groups. Each group of teeth was etched with different acid concentration (3.7%, 18.5% and 37%). Subsequently, shear bond strength of orthodontic brackets was tested in Universal Testing Machine. Results and discussion:The lowest mean bond strength (7.59 MPa) was recorded in the teeth etched with 3.7% phosphoric acid. While the highest mean SBS was found in the group of teeth etched with 37% phosphoric acid (10.35). The group of teeth etched with 18.5% phosphoric acid represented intermediate SBS value, which was 9.16 MPa. Teeth etched with 37% phosphoric acid showed higher adhesion at the enamel/resin interface, while teeth etched with 3.7% phosphoric acid had higher adhesion at the resin/bracket interface. Findings for the group of teeth etched with 18.5% phosphoric acid were in between. Conclusions: We consider that lower concentrations of acid should be used during bracket bonding. АпстрактВовед: Нагризувањето на емајлот на забот е важна и неопходна фаза во протоколот на поставување на фиксниот ортодонтски апарат. За подготовка на емајловата површина и врзување на брекетот за забот може да се користи различното време на нагризување и различната концентрација на киселина. Општо земено, колку е подолго времето на нагризување и поголема концентрацијата на киселина, толку е појака врската меѓу брекетот и емајлот на забот. Сепак, неодамнешните студии се фокусираат на намалување на концентрацијата на киселината за нагризување. Цел на студијата: да се процени штетата предизвикана од различни концентрации на киселина на емајлот, да се утврди влијанието на концентрацијата на киселината врз јачината на врската меѓу забот и брекетот, да се одреди концентрацијата на киселината со која би се постигнала оптимална јачина на врската со минимално оштетување на емајлот. Материјал и метод: Материјалот за оваа Ин Витро студија го сочинуваат 30 здрави премолари (екстрахирани од ортодонтски причини, во цел на екстракциона ортодонтска терапија), поделени во 3 групи. Кај секоја група беше извршено нагризување со три различни концентрации на киселина (3,7%; 18,5% и 37%). Последователно, јачината на вр...

Introduction:Etching in orthodontics is the most important phase of brackets bonding, and failure to achieve proper bonding may result in poor orthodontic results. Thus, for many years, many attempts have been made to achieve the best etching method in order to maximize orthodontic therapy effect, and on the other hand, to minimize unnecessary re-bonding of failed brackets during orthodontic therapy. Failure to do so leads to prolonged orthodontic therapy including complications like unnecessary checkups at orthodontic office. Aim of the study: The impact of different etching duration on enamel surface; the evaluation of bond strength regarding different etching duration; the optimal etching duration for bond strength. Establishing laboratory evidence of the minimum etching duration of enamel to provide effective retention of orthodontic brackets. Material and methods: Thirty sound premolar teeth (extracted for orthodontic reasons) were divided into three groups. Each group of teeth was etched for 10, 30 and 60 seconds. Shear bond strength and ARI Index were evaluated. Results and discussion: The highest bond strength was found among the group of teeth etched for 30 seconds (9.89 MPa). However similar results were found in the group of teeth etched for 10 seconds (9.44 MPa). The group of teeth etched for 60 seconds exhibited the lowest SBS (8.16 MPa). The larger number of teeth exhibited ARI index 1 (10 teeth). Followed by the equal number of teeth belonging to ARI index 0 and 2. (7 each). Lowest score was recorded with ARI index 3. Conclusions: We consider that 10 seconds of etching is suitable in daily orthodontic clinical practice. АпстрактВовед: Нагризувањето на емајловата површина е многу значајна фаза во поставувањето на брекетите од фиксниот ортодонтски апарат, и може да биде причина за неуспех во ортодонтскиот третман поради воспоставување на слаба врска меѓу забот и брекетот и да влијае на јачината на силата. Затоа низа години наназад се прават обиди да се постигне најдобриот метод за нагризување со цел да се подобри ефектот од нагризувањето и да се минимизира непотребното повторување на постапката за врзување на брекетот со емајлот на забот со што се успорува и компромитира текот на ортодонтскиот третман, што вклучува и дополнителни прегледи и пролонгирање на времетраењето на третманот. Цел: Да се испита влијанието на различно време на нагризување на емајлот, да се изврши проценка на јачината на врската меѓу брекетот и емајлот на забот во зависност од различното време на нагризување и да се утврди оптималното време на нагризување, преку лабораториски докази за минимално потребно време од нагризување на емајлот како би се обезбедила ефикасна врска помеѓу брекетот и емајлот на забот. Материјал и метод: Испитувањето е извршено на 30 здрави премолари (екстрахирани од ортодонтски причини, во цел екстракциона ортодонтска терапија) поделени во три групи. Кај секоја група беше изведено нагризување во траење од 10, 30 и 60 секунди. Извршена е проценка на трите различни времетраења на нагризување на емајлот врз ј...