The mechanical properties of solution treated ASTM F-75 alloys with various carbon contents have been studied. Alloys cast under the same conditions were subjected to solution treatment for several periods and then their tensile properties were evaluated. In the as-cast conditions, the alloys exhibited higher strength values with increasing carbon content whereas their ductility was not significantly affected. For the solution treated alloys, the variation of the strength was characterized by a progressive increase for short treatment times until a maximum value was achieved, which was followed by a diminution in this property for longer treatment times. This behavior was more accentuated for the case of the alloys with medium carbon contents, which also exhibited the highest values of strength. Furthermore, the alloy's ductility was enhanced progressively with increasing solution treatment time. This improvement in ductility was significantly higher for the medium carbon alloys compared with the rest of the studied alloys. Thus, high and low carbon contents in solution treated ASTM F-75 alloys did not produced sufficiently high tensile properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.