Additive manufacturing allows for the production of complex parts with minimum material waste, offering an effective technique for fabricating permanent magnets which frequently involve critical rare earth elements. In this report, we demonstrate a novel method - Big Area Additive Manufacturing (BAAM) - to fabricate isotropic near-net-shape NdFeB bonded magnets with magnetic and mechanical properties comparable or better than those of traditional injection molded magnets. The starting polymer magnet composite pellets consist of 65 vol% isotropic NdFeB powder and 35 vol% polyamide (Nylon-12). The density of the final BAAM magnet product reached 4.8 g/cm3, and the room temperature magnetic properties are: intrinsic coercivity Hci = 688.4 kA/m, remanence Br = 0.51 T, and energy product (BH)max = 43.49 kJ/m3 (5.47 MGOe). In addition, tensile tests performed on four dog-bone shaped specimens yielded an average ultimate tensile strength of 6.60 MPa and an average failure strain of 4.18%. Scanning electron microscopy images of the fracture surfaces indicate that the failure is primarily related to the debonding of the magnetic particles from the polymer binder. The present method significantly simplifies manufacturing of near-net-shape bonded magnets, enables efficient use of rare earth elements thus contributing towards enriching the supply of critical materials.

Herein we report on the synthesis and characterization of MXene–polyacrylamide (PAM) nanocomposite films. The as-prepared composites are flexible and the conductivity was increased significantly to 3.3 × 10−2S m−1with only 6 wt% MXene loading.

No abstract

A series of F‐substituted Na2/3Ni1/3Mn2/3O2−xFx (x = 0, 0.03, 0.05, 0.07) cathode materials have been synthesized and characterized by solid‐state 19F and 23Na NMR, X‐ray photoelectron spectroscopy, and neutron diffraction. The underlying charge compensation mechanism is systematically unraveled by X‐ray absorption spectroscopy and electron energy loss spectroscopy (EELS) techniques, revealing partial reduction from Mn4+ to Mn3+ upon F‐substitution. It is revealed that not only Ni but also Mn participates in the redox reaction process, which is confirmed for the first time by EELS techniques, contributing to an increase in discharge specific capacity. The detailed structural transformations are also revealed by operando X‐ray diffraction experiments during the intercalation and deintercalation process of Na+, demonstrating that the biphasic reaction is obviously suppressed in the low voltage region via F‐substitution. Hence, the optimized sample with 0.05 mol f.u.−1 fluorine substitution delivers an ultrahigh specific capacity of 61 mAh g−1 at 10 C after 2000 cycles at 30 °C, an extraordinary cycling stability with a capacity retention of 75.6% after 2000 cycles at 10 C and 55 °C, an outstanding full battery performance with 89.5% capacity retention after 300 cycles at 1 C. This research provides a crucial understanding of the influence of F‐substitution on the crystal structure of the P2‐type materials and opens a new avenue for sodium‐ion batteries.

We have investigated the temperature and magnetic field dependence of the Hall coefficient of two wellcharacterized superconducting MgB 2 films (T c0 ϭ38.0 K) in both the normal and superconducting states. Our results show that the normal-state Hall coefficient R H is positive and increases with decreasing temperature, independent of the applied magnetic field ͑to 8 T͒. We find that R H Ϫ1 ϰT(40-300 K) and cot H ϰT 2 (100-300 K). As the sample is cooled below T c (H), R H decreases rapidly with temperature and changes sign before it reaches zero. The position and magnitude at which R H shows a minimum depends on the applied field.