We address room-temperature conductivities of chemically grown silver films. Disordered, granular silver films are grown using a modified Tollens reaction. Thick, polycrystalline films are transparent at visible wavelengths, with crystallinity similar to that of silver powders. The measured conductivities are close to those measured by I. V. Antonets, L. N. Kotov, S. V. Nekipelov, and Ye. A. Golubev, Tech. Phys. 49, 306 (2004) in amorphous silver films, however the thickness where bulk conductivity is reached is anomalously high. While measured resistance values do not obey a scaling relation in thickness, accounting for the films’ structural porosity through geometrical rescaling of the thickness leads to emergence of the well-known percolation power-law scaling, albeit that of two-dimensional percolating films.

Neste trabalho, apresenta-se o estudo experimental em escala laboratorial e industrial da incorporação de resíduo do tratamento de Drenagem Ácida de Mina (DAM) na formulação de massa de cerâmica vermelha, com substituição parcial das argilas. Foram realizados algumas análises e ensaios nas amostras dos blocos cerâmicos: análise dilatométrica a verde, absorção de água, resistência à compressão, eflorescência de sais solúveis e emissões atmosféricas (MP e SOx). Os resultados das análises nos corpos de prova ensaiados indicam aumento de resistência a compressão. Os ensaios de eflorescência de sais solúveis indicam maior intensidade de cristalização de sais solúveis na superfície dos corpos de prova e blocos cerâmicos à medida que se aumenta o percentual de resíduo. As análises realizadas nos blocos cerâmicos ensaiados em escala industrial, recomendam uma proporção de até 2,5% de resíduo na massa cerâmica.