High temperature gas reactor experiments create unique challenges for thermocouple-based temperature measurements. As a result of the interaction with neutrons, the thermoelements of the thermocouples undergo transmutation, which produces a time-dependent change in composition and, as a consequence, a time-dependent drift of the thermocouple signal. This drift is particularly severe for high temperature platinumrhodium thermocouples (Types S, R, and B) and tungstenrhenium thermocouples (Type C). For lower temperature applications, previous experiences with Type K thermocouples in nuclear reactors have shown that they are affected by neutron irradiation only to a limited extent. Similarly, Type N thermocouples are expected to be only slightly affected by neutron fluence. Currently, the use of these nickel-based thermocouples is limited when the temperature exceeds 1000°C due to drift related to phenomena other than nuclear irradiation. High rates of open-circuit failure are also typical. Over the past 10 years, three long-term Advanced Gas Reactor experiments have been conducted with measured temperatures ranging from 700°C-1200°C. A variety of standard Type N and specialty thermocouple designs have been used in these experiments with mixed results. A brief summary of thermocouple performance in these experiments is provided. Most recently, out-of-pile testing has been conducted on a variety of Type N thermocouple designs at the following (nominal) temperatures and durations: 1150°C and 1200°C for 2,000 hours at each temperature, followed by 200 hours at 1250°C and 200 hours at 1300°C. The standard Type N design utilizes high purity, crushed MgO insulation and an Inconel 600 sheath. Several variations on the standard Type N design were tested, including a Haynes 214 alloy sheath, spinel (MgAl 2 O 4 ) insulation instead of MgO, a customized sheath developed at the University of Cambridge, and finally a loose assembly thermocouple with hard-fired alumina insulation and a molybdenum sheath. The most current version of the High Temperature Irradiation Resistant Thermocouple, based on molybdenum/niobium alloys and developed at Idaho National Laboratory, was also tested.

No abstract

No abstract

A new nickel based thermocouple for high temperature applications in gas turbines has been devised at the Department of Material Science and Metallurgy of the University of Cambridge. This paper describes the new features of the thermocouple, the drift tests on the first prototype, and compares the behavior of the new sensor with conventional mineral insulated metal sheathed Type K thermocouples: the new thermocouple has a significant improvement in terms of drift and temperature capabilities. Metallurgical analysis has been undertaken on selected sections of the thermocouples exposed at high temperatures, which rationalizes the reduced drift of the new sensor. A second prototype will be tested in subsequent research, from which further improvements in drift and temperature capabilities are expected.

The Advanced Gas Reactor-5/6/7 (AGR-5/6/7) experiment is the fourth and final experiment in the AGR experiment series and will serve as the formal fuel qualification test for the TRISO fuels under development by the U.S. Department of Energy. Certain locations in this experiment reach temperatures higher than any of the previous AGR tests, up to 1500°C. Such extreme temperatures create unique challenges for thermocouple-based temperature measurements. High-temperature platinum-rhodium thermocouples (Types S, R, and B)and tungsten-rhenium thermocouples (Type C) suffer rapiddecalibration due to transmutation of the thermoelements fromneutron absorption. For lower temperature applications, previousexperience with Type K thermocouples in nuclear reactors haveshown that they are affected by neutron irradiation only to alimited extent. Similarly, Type N thermocouples, which are morestable than Type K at high temperatures, are only slightly affectedby neutron fluence. Until recently, the use of these nickel-basedthermocouples was limited when the temperature exceeds 1050°Cdue to drift related to phenomena other than nuclear irradiation.Recognizing the limitations of existing thermometery to measuresuch high temperatures, the sponsor of the AGR-5/6/7 experimentsupported a development and testing program for thermocouplescapable of low drift operation at temperatures above 1100°C. High Temperature Irradiation Resistant Thermocouples (HTIR-TCs)based on molybdenum/niobium thermoelements have been underdevelopment at Idaho National Laboratory (INL) since circa 2004. A step change in accuracy and long-term stability of thisthermocouple type has been achieved as part of the AGR-5/6/7thermometry development program. Additionally, long-termtesting (9000+ hrs) at 1250°C of the Type N thermocouplesutilizing a customized sheath developed at the University ofCambridge has been completed with low drift results. Both theimproved HTIR and the Cambridge Type N thermocouple typeshave been incorporated into the AGR-5/6/7 test, which beganirradiation in February 2018 in INL’s Advanced