Abstract. Current challenges like increasing safety standards and reducing fuel consumption motivate lightweight construction in modern car bodies. Besides using lightweight workpiece materials like aluminum, hot stamping has been established as a key technology for producing safety relevant components. Producing hot stamped parts out of ultra-high strength steels offers the possibility to improve the crash performance. At the same time the weight of car structure is reduced by using thinner sheet thicknesses. In order to avoid oxide scale formation and ensure corrosion protection, AlSi coatings are commonly deposited on the sheet surfaces used for direct hot stamping. This workpiece coating has a critical impact on the tribological conditions within the forming process and, as a consequence, influences the quality of hot stamped parts as well as tool wear. AlSi coatings have been identified as major reason for adhesive wear, which represents the main wear mechanism in hot stamping. Within this study, the influence of the process parameters on adhesive wear are investigated in dependency of workpiece and tool temperatures, drawing velocities and contact pressures. The tribological behavior is analyzed based on strip drawing experiments under direct hot stamping conditions. The experiments are performed with AlSi coated 22MnB5 in contact with the hot working tool steel 1.2367. For analyzing the amount of adhesion on the friction jaws, the surfaces are characterized by optical measurements. The experiments indicate that higher workpiece temperatures cause severe adhesive wear on the tool surface, while an increase of drawing velocity or contact pressure led to reduced adhesion. The measured friction coefficients decreased with rising amount of adhesion and remained at a constant level after a certain adhesive layer was built up on the tool surface.