In this paper, we studied some ferroelectric properties of archetypal oxide uniaxial ferroelectric single crystals of Pb5Ge3O11 modified by Ba ions. They include dielectric, DSC, ferroelectric polarization, and electrocaloric effect (ECE) measurements. The measurements show that increasing Ba doping considerably influences all the measured parameters, mainly by lowering the Curie temperature, gradually diffusing the phase transition, and decreasing values of polarization as well as the coercive field. The decrease in overall ECE is influenced by decreasing polarization. Compared with the pure PGO single crystals, this decrease is from 1.2 K to 0.2 K. However, the effect of diffusing the phase transition increases the range of its occurrence (up to 30 K), which might be beneficial in applications.

Ferroelectric ceramics BaTiO3:x%Eu (x = 0, 0.1, 1, 2, 3) were synthesized by a conventional method. Structural investigation confirmed that all ceramics possessed tetragonal (P4mm) symmetries at room temperature for the undoped ceramics as well as for the doped ceramics. Furthermore, a slight downshifting of the Curie temperature (TC) with an increasing Eu3+ doping amount has been noted. The Raman spectra unveiled the existence of new modes for higher-doped BaTiO3:x%Eu (BTEx) which are related to local disorders and defects. The ferroelectric properties were found to depend on both doping and the microstructure. The electrocaloric effect was also studied for those ceramics. It was observed that ΔT decreases with doping; however, the temperature range of its occurrence widens considerably.