A new type of nanocellulosic material has been prepared by high-pressure homogenization of carboxymethylated cellulose fibers followed by ultrasonication and centrifugation. This material had a cylindrical cross-section as shown by transmission electron microscopy with a diameter of 5-15 nm and a length of up to 1 microm. Calculations, using the Poisson-Boltzmann equation, showed that the surface potential was between 200 and 250 mV, depending on the pH, the salt concentration, and the size of the fibrils. They also showed that the carboxyl groups on the surface of the nanofibrils are not fully dissociated until the pH has reached pH = approximately 10 in deionized water. Calculations of the interaction between the fibrils using the Derjaguin-Landau-Verwey-Overbeek theory and assuming a cylindrical geometry indicated that there is a large electrostatic repulsion between these fibrils, provided the carboxyl groups are dissociated. If the pH is too low and/or the salt concentration is too high, there will be a large attraction between the fibrils, leading to a rapid aggregation of the fibrils. It is also possible to form polyelectrolyte multilayers (PEMs) by combining different types of polyelectrolytes and microfibrillated cellulose (MFC). In this study, silicon oxide surfaces were first treated with cationic polyelectrolytes before the surfaces were exposed to MFC. The build-up of the layers was monitored with ellipsometry, and they show that it is possible to form very well-defined layers by combinations of MFC and different types of polyelectrolytes and different ionic strengths of the solutions during the adsorption of the polyelectrolyte. A polyelectrolyte with a three-dimensional structure leads to the build-up of thick layers of MFC, whereas the use of a highly charged linear polyelectrolyte leads to the formation of thinner layers of MFC. An increase in the salt concentration during the adsorption of the polyelectrolyte results in the formation of thicker layers of MFC, indicating that the structure of the adsorbed polyelectrolyte has a large influence on the formation of the MFC layer. The films of polyelectrolytes and MFC were so smooth and well-defined that they showed clearly different interference colors, depending on the film thickness. A comparison between the thickness of the films, as measured with ellipsometry, and the thickness estimated from their colors showed good agreement, assuming that the films consisted mainly of solid cellulose with a refractive index of 1.53. Carboxymethylated MFC is thus a new type of nanomaterial that can be combined with oppositely charged polyelectrolytes to form well-defined layers that may be used to form, for example, new types of sensor materials.

No abstract

The kinetics of kraft lignin (KL) aggregation at alkaline conditions was studied by quasi-elastic light scattering (QELS) and turbidity measurements. Stability ratios (W) for KL were obtained at 70 °C and various concentrations of sodium chloride. By analyzing the early-time evolution data of aggregate growth obtained from QELS, fractal dimensions of flocs formed in both reaction-limited cluster-cluster aggregation regimes and diffusion-limited cluster-cluster aggregation regimes were determined. Correlations between the fractal dimension and the W-ratio were found in accordance to recent studies of a system containing monodisperse polystyrene colloids. By cryogenic transmission electron microscopy, the fractality of KL aggregate structures in the system was also shown. It was seen from stability studies of KL solutions that the effects of specific co-and counterions follow the Hofmeister series. From the outcome of the investigation, different modes of aggregation occurring in a KL system are proposed. Starting from the macromolecular state of KL and evolving through larger aggregates, the KL clusters finally exhibit a supramolecular structure similar to what earlier has been proposed for native softwood lignin.