This study evaluated the influence of polydopamine treatment on the surface properties and bond strength of yttria‐stabilised tetragonal zirconia polycrystal (Y‐TZP). Sixty‐three zirconia blocks (10 × 10 × 2 mm) were randomly divided into three groups defined by surface treatment: (i) control group (C), (ii) grit‐blasted with 110 μm alumina particles (GB), and (iii) polydopamine (PDA) coating. The surfaces of specimens subjected to different treatments were investigated by X‐ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and water contact angle measurements. After the surface treatments, the specimens were cemented to resin composite cylinders. After bonding, the shear bond strength of the ceramic to the resin was measured, and the failure mode of each specimen was analysed using a stereomicroscope. The results indicated that the shear bond strength is highest for the GB treatment and lowest for the controls. However, the difference between groups GB and PDA was not statistically significant. In the control group, adhesive failure was predominant, whereas in the treatment groups, mixed mode failure was predominant. The pre‐treatment of Y‐TZP ceramic with the polydopamine coating might improve the bond strength of the resin cement to the zirconia ceramic.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.