This letter reports a β-SiAlON:Eu2+ green phosphor with the composition of Eu0.00296Si0.41395Al0.01334O0.0044N0.56528. The phosphor powder exhibits a rod-like morphology with the length of ∼4μm and the diameter of ∼0.5μm. It can be excited efficiently over a broad spectral range between 280 and 480 nm, and has an emission peak at 535 nm with a full width at half maximum of 55 nm. It has a superior color chromaticity of x=0.32 and y=0.64. The internal and external quantum efficiencies of this phosphor is 70% and 61% at λex=303nm, respectively. This newly developed green phosphor has potential applications in phosphor-converted white LEDs.

In this letter, a yellow oxynitride phosphor α-SiAlON with compositions of Ca0.625EuxSi0.75−3xAl1.25+3xOxN16−x (Ca-α-SiAlON:Eu, x=0–25) was prepared by gas pressure sintering. The diffuse reflection spectrum, photoluminescence spectrum, and chromaticity of the powder phosphors were presented. It absorbs light efficiently in the UV–visible spectral region, and shows a single intense broadband emission at 583–603nm. This phosphor may become a good candidate for creating white light, typically warm white light, when coupled to a blue light-emitting diode (λem=450nm).

ChemInform is a weekly Abstracting Service, delivering concise information at a glance that was extracted from about 200 leading journals. To access a ChemInform Abstract, please click on HTML or PDF.