Basic oxygen furnace (BOF) slag was modified by adding 3.5% SiO2 and holding at 1673 K for 0, 5, 40, 90, 240, or 360 min. Kilo-scale modification was also carried out. The growth, stratification, and liberation of P-rich C2S in the modified slag were investigated. The optimum holding time was 240 min, and 90% of C2S grains were above 30 μm in size. The phosphorus content increased with holding time, and after modification, the phosphorus content in C2S was nearly three times higher than that in the original slag (2.23%). Obvious stratification of C2S was observed in the kilo-scale modification. Upper C2S particles with a relatively larger size of 20–110 μm was independent of RO (FeO-MgO-MnO solid solution) and spinel, which is favorable for liberation. Lower C2S was less than 3 μm and was embedded in spinel, which is not conducive to liberation. The content of phosphorus in upper C2S (6.60%) was about twice that of the lower (3.80%). After grinding, most of the upper C2S existed as free particles and as locked particles in the lower. The liberation degree of C2S in the upper increased with grinding time, from 86.02% to 95.92% in the range of 30–300 s, and the optimum grinding time was 180 s. For the lower slag grinding for 300 s, the liberation degree of C2S was 40.07%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.