Industries demand stringent requirements towards economical machining without hindering the surface quality while cutting high carbon high chromium (HcHcr) steel. Electrical discharge machining (EDM) of HcHcr steel aims at reducing machining cost (i.e., maximize material removal rate (MRR) and minimize tool wear rate (TWR)) with good surface quality (i.e., minimize surface roughness (SR)). A comparative study was carried out on EDM of HcHcr D2 steel (DIN EN ISO 4957) by applying Taguchi L18 experimental design considering different electrode materials (copper, graphite, and brass), dielectric fluids (distilled water and kerosene), peak current, and pulse-on-time. The process performances were analyzed with respect to material removal rate, surface roughness, and tool wear rate. Pareto analysis of variance was employed to estimate the significance of the process variables and their optimal levels for achieving lower SR and TWR and higher MRR. Hybrid Taguchi-CRITIC-Utility and Taguchi-PCA-Utility methods were implemented to determine the optimal EDM parameters. Higher MRR of 0.0632 g/min and lower SR of 1.68 µm and TWR of 0.012 g/min was attained by graphite electrode in presence of distilled water as dielectric fluid compared to the brass and copper. Additionally, a metallographic analysis was carried out to study the surface integrity on the machined surfaces. Micrographic analysis of the optimal conditions showed lower surface roughness and fewer imperfections (lesser impression, waviness surface, and micro-cracks) compared to worst conditions.

The development of the best properties in polyester composite from pineapple leaf fiber (PALF) as a reinforcing material is a subject of interest. The properties of PALF are reliant upon fiber length, wherein technical difficulties in production of long fibers and processing for better characteristics in polyester composites possess inherent challenges. The PALFs are subjected to silane treatment for altering fiber properties. This research attempts to analyze the impact of silane-treated PALF with varying fiber lengths (5, 10, 15, 20, and 25 mm) on the performance of natural fiber composites (NFC) properties. Open mold and hand lay-up techniques were employed to develop the polyester composites. The prepared PALF-based polyester composites were examined for different properties (impact, flexural, tensile strength, and wear rate). Coefficient of friction and wear studies are performed on the prepared composites subjected to different loads (10, 20, and 30 N) via a pin on disc test rig. Polymer composite fracture surfaces were analyzed to observe the interfacial bonding between fibers and matrix via scanning electron microscopy (SEM). SEM results showed that the application of silane treatment resulted in better surface topography (fiber length of 5–10 mm showed smooth surface resulted in crack proliferation possessing low fracture toughness of 15–32 MPa; whereas a 15–20 mm fiber length resulted in better fiber–matrix bonding, improving the fracture toughness from 42–55 MPa) as a result of change in chemical structure in PALF. The 20 mm length of PALF resulted in better properties (flexural, tensile, impact, and wear resistance) which are attributed to fiber–matrix interfacial bonding. These properties ensure the developed polymer composites can be applied to walls, building insulation, and artificial ceilings.

Zinc (Zn) is one of the five most widely consumed metals in the world. Indeed, more than 50% of all the zinc produced is used in zinc-galvanizing processes to protect steel from corrosion. Zn-based coatings have the potential for use as a corrosion-resistant barrier, but their wider use is restricted due to the poor mechanical properties of Zn that are needed to protect steel and other metals from rusting. The addition of other alloying elements such as Ni (Nickle) and WC (Tungsten Carbide) to Zn coating can improve its performance. This study investigates, the corrosion performance of Zn–Ni coating and Zn–Ni–WC composite nanocoatings fabricated on mild steel substrate in an environmentally friendly bath solution. The influence of WC nanoparticles on Zn–Ni deposition was also investigated. The surface morphologies, texture coefficients via XRD (X-ray diffraction), SEM (Scanning Electron Microscopy), and EDS (Energy-dispersive X-ray spectroscopy) were analyzed. The electrochemical test such as polarization curves (PC) and electrochemical impedance spectroscopy (EIS) resulted in a corrosion rate of 0.6948 Å/min for Zn–Ni–WC composite nanocoating, and 1.192 Å/min for Zn–Ni coating. The results showed that the Zn–Ni–WC composite nanocoating reduced the corrosion rate by 41.71% and showed an 8.56% increase in microhardness compared to the hardness of the Zn–Ni coating. These results are augmented to better wettable characteristics of zinc, which developed good interfacial metallurgical adhesion amongst the Ni and WC elements. The results of the novel Zn–Ni–WC nanocomposite coatings achieved a great improvement of mechanical property and corrosion protection to the steel substrate surface.