The microstructure evolution, superplasticity, and room temperature mechanical properties of Ti-4%Al-1%V-3%Mo alloys modified with 0.01-2 wt.% boron were investigated. Increasing the boron content from 0 to 0.1 wt.% effectively refined prior β-grains, reducing a mean grain size from ~700 µm to ~210 µm. Whiskers of the TiB phase with a size in a range of 0.7-2.9 µm were observed after solidification and thermomechanical processing. Alloys with 0.01-0.1 wt.% boron exhibited similar superplastic elongations and strain rate sensitivity coefficient m of 0.4-0.5 at a strain rate of 1×10-3 s-1 and the elongation to failure decreased from 1000% at 875°С to 400-500% at 700°С. Along with this, the minor boron addition effectively decreased flow stress values, especially at 775 °C, that was explained by the acceleration of the recrystallization and globularization of the microstructure at the initial stage of deformation. Recrystallization-induced decrease in yield strength from 770 MPa to 680 MPa was observed with an increase in boron content from 0 to 0.1 wt.%. Heat treatment increased post-forming strength characteristics for the alloys with 0.01-0.1 wt.% boron by 90–140 MPa without ductility reduction. Alloys with 1-2 wt.% B demonstrated the opposite behavior. The grain refinement effect was not revealed, and prior β grain sizes were ~670-750 µm after solidification. Thermomechanical processing promoted the fragmentation of boride whiskers and the formation of near-spherical particles with a size of ~1 μm for the alloy with a eutectic concentration of 2 wt.% B. A high fraction of borides, ~5-11%, in the alloys with 1-2 wt.% B deteriorated the superplastic properties and drastically decreased ductility at room temperature. The alloy with 2 wt.% B demonstrated non-superplastic behavior and a low level of mechanical properties, meanwhile, the alloy with 1% boron exhibited high-temperature superplasticity at 875 °C with elongation of ~500%, and yield strength of 830 MPa, ultimate tensile strength of 1020 MPa at a room temperature after 100% of superplastic deformation.
The paper studies the influence of 0.5–1.8 wt.% Ni alloying on the superplasticity, microstructural evolution, and dynamic grain growth effect in a temperature range of 625–775 °C and room temperature mechanical properties of two-phase Ti-Al-Mo-V alloys. Due to a decrease in β transus and an enhancement in the alloy diffusivity, an increase in Ni content significantly improved superplasticity. The Ni-modified alloys exhibited 1.5–3-fold lower flow stress, a 2.5–3-fold greater elongation to failure, and 1.4–1.7-fold higher strain rate sensitivity m coefficient compared to the Ni-free alloy. An intermetallic Ti2Ni compound precipitated in the 1.8 wt.% Ni-modified alloy during low-temperature deformation at 700 °C and decreased superplastic properties. The Ti-4Al-3Mo-1V-0.1B alloy with 0.9 wt.% Ni exhibited a good combination of the superplastic behavior and room-temperature mechanical properties: an elongation to failure of 500–900% at a low-temperature range of 625–775 °C and constant strain rate of 1 × 10−3 s−1 and a yield strength of 885 MPa and ultimate tensile strength of 1020 MPa after pre-straining for 100% in a superplastic regime and strengthening heat treatment.
The decrease of superplastic forming temperature and improvement of post-forming mechanical properties are important issues for titanium-based alloys. Ultrafine-grained and homogeneous microstructure are required to improve both processing and mechanical properties. This study focuses on the influence of 0.01–2 wt.% B (boron) on the microstructure and properties of Ti-4Al-3Mo-1V (wt.%) alloys. The microstructure evolution, superplasticity, and room temperature mechanical properties of boron-free and boron-modified alloys were investigated using light optical microscopy, scanning electron microscopy, electron backscatter diffraction, X-ray diffraction analysis, and uniaxial tensile tests. A trace addition of 0.01 to 0.1 wt.% B significantly refined prior β-grains and improved superplasticity. Alloys with minor B and B-free alloy exhibited similar superplastic elongations of 400–1000% in a temperature range of 700–875 °C and strain rate sensitivity coefficient m of 0.4–0.5. Along with this, a trace boron addition provided a stable flow and effectively reduced flow stress values, especially at low temperatures, that was explained by the acceleration of the recrystallization and globularization of the microstructure at the initial stage of superplastic deformation. Recrystallization-induced decrease in yield strength from 770 MPa to 680 MPa was observed with an increase in boron content from 0 to 0.1%. Post-forming heat treatment, including quenching and ageing, increased strength characteristics of the alloys with 0.01 and 0.1% boron by 90–140 MPa and insignificantly decreased ductility. Alloys with 1–2% B exhibited an opposite behavior. For the high-boron alloys, the refinement effect of the prior β-grains was not detected. A high fraction of borides of ~5–11% deteriorated the superplastic properties and drastically decreased ductility at room temperature. The alloy with 2% B demonstrated non-superplastic behavior and low level of strength properties; meanwhile, the alloy with 1% B exhibited superplasticity at 875 °C with elongation of ~500%, post-forming yield strength of 830 MPa, and ultimate tensile strength of 1020 MPa at room temperature. The differences between minor boron and high boron influence on the grain structure and properties were discussed and the mechanisms of the boron influence were suggested.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2025 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.