The preparation method greatly influences morphology, acid–base properties and performance of SiO2–MgO catalysts. Wet-kneaded catalysts possess an improved distribution, proximity and strength of acidic-basic sites, thus leading to higher butadiene yields.

Silica-magnesia (Si/Mg=1:1) catalysts were studied in the one-pot conversion of ethanol to butadiene. The catalyst synthesis method was found to greatly influence morphology and performance, with materials prepared through wet-kneading performing best both in terms of ethanol conversion and butadiene yield. Detailed characterization of the catalysts synthesized through co-precipitation or wet-kneading allowed correlation of activity and selectivity with morphology, textural properties, crystallinity, and acidity/basicity. The higher yields achieved with the wet-kneaded catalysts were attributed to a morphology consisting of SiO2 spheres embedded in a thin layer of MgO. The particle size of the SiO2 catalysts also influenced performance, with catalysts with smaller SiO2 spheres showing higher activity. Temperature-programmed desorption (TPD) measurements showed that best butadiene yields were obtained with SiO2-MgO catalysts characterized by an intermediate amount of acidic and basic sites. A Hammett indicator study showed the catalysts' pK(a) value to be inversely correlated with the amount of dehydration by-products formed. Butadiene yields could be further improved by the addition of 1 wt% of CuO as promoter to give butadiene yields and selectivities as high as 40% and 53%, respectively. The copper promoter boosts the production of the acetaldehyde intermediate changing the rate-determining step of the process. TEM-energy-dispersive X-ray (EDX) analyses showed CuO to be present on both the SiO2 and MgO components. UV/Vis spectra of promoted catalysts in turn pointed at the presence of cluster-like CuO species, which are proposed to be responsible for the increased butadiene production.

In single-site olefin polymerization catalysis, a large excess of cocatalyst is often required for the generation of highly active catalysts, but the reason for this is unclear. In this work, fundamental insight into the multifaceted role of cocatalyst methylaluminoxane (MAO) in the activation, deactivation, and stabilization of group 4 metallocenes in the immobilized single-site olefin polymerization catalyst was gained. Employing probe molecule FT-IR spectroscopy, it was found that weak Lewis acid sites, inherent to the silica-supported MAO cocatalyst, are the main responsible species for the genesis of active metallocenes for olefin polymerization. These weak Lewis acid sites are the origin of AlMe2+ groups. Deactivation of metallocenes is caused by the presence of silanol groups on the silica support. Interaction of the catalyst precursor with these silanol groups leads to the irreversible formation of inactive metallocenes. Importantly, a high concentration of MAO (14 wt% Al) on the silica support is necessary to keep the metallocenes immobilized, hence preventing metallocene leaching and consequent reactor fouling. Increasing the loading of the MAO cocatalyst leads to larger amounts of AlMe2+, fewer silanol groups, and less metallocene leaching, which all result in higher olefin polymerization activity.

A major cause of supported metal catalyst deactivation is particle growth by Ostwald ripening. Nickel catalysts, used in the methanation reaction, may suffer greatly from this through the formation of [Ni(CO)4 ]. By analyzing catalysts with various particle sizes and spatial distributions, the interparticle distance was found to have little effect on the stability, because formation and decomposition of nickel carbonyl rather than diffusion was rate limiting. Small particles (3-4 nm) were found to grow very large (20-200 nm), involving local destruction of the support, which was detrimental to the catalyst stability. However, medium sized particles (8 nm) remained confined by the pores of the support displaying enhanced stability, and an activity 3 times higher than initially small particles after 150 h. Physical modeling suggests that the higher [Ni(CO)4 ] supersaturation in catalysts with smaller particles enabled them to overcome the mechanical resistance of the support. Understanding the interplay of particle size and support properties related to the stability of nanoparticles offers the prospect of novel strategies to develop more stable nanostructured materials, also for applications beyond catalysis.