Antibacterial bonding agents could combat recurrent caries at the tooth-composite margins. The objectives of this study were to develop novel antibacterial dentin primers containing quaternary ammonium dimethacrylate (QADM) and nanoparticles of silver (NAg), and to investigate the effects on dentin bond strength and dental plaque microcosm biofilms for the first time. Scotchbond Multi-Purpose ("SBMP") bonding agent was used. QADM and NAg were incorporated into SBMP primer, yielding 4 primers: SBMP primer (control), control + 10% QADM (mass), control + 0.05% NAg, and control + 10% QADM + 0.05% NAg. Human saliva was collected to grow microcosm biofilms. The NAg particle size (mean ± SD; n = 100) was 2.7 ± 0.6 nm. Dentin shear bond strengths (n = 10) with human third molars were approximately 30 MPa for all groups (p > 0.1). QADMNAg-containing primer increased the bacteria inhibition zone by 9-fold, compared with control primer (p < 0.05). QADM-NAg-containing primer reduced lactic acid production and colony-forming units of total micro-organisms, total streptococci, and mutans streptococci by an order of magnitude. In conclusion, novel QADM-NAg-containing primers were strongly antibacterial without compromising dentin bond strength, and hence are promising to inhibit biofilms and secondary caries. The processing method of incorporating QADM and NAg together into the same primer produced the strongest antibacterial effect, which could have a wide applicability to other bonding systems.KEY WOrDs: antibacterial dentin primer, quaternary ammonium salt, dental biomaterials, bond strength, dental plaque microcosm biofilm, caries inhibition.

Objectives Antibacterial bonding agents are promising to hinder the residual and invading bacteria at the tooth-restoration interfaces. The objectives of this study were to develop an antibacterial bonding agent by incorporation of quaternary ammonium dimethacrylate (QADM) and nanoparticles of silver (NAg), and to investigate the effect of QADM-NAg adhesive and primer on dentin bond strength and plaque microcosm biofilm response for the first time. Methods Scotchbond Multi-Purpose adhesive and primer were used as control. Experimental adhesive and primer were made by adding QADM and NAg into control adhesive and primer. Human dentin shear bond strengths were measured (n = 10). A dental plaque microcosm biofilm model with human saliva as inoculum was used to investigate biofilm metabolic activity, colony-forming unit (CFU) counts, lactic acid production, and live/dead staining assay (n = 6). Results Adding QADM and NAg into adhesive and primer did not compromise the dentin shear bond strength which ranged from 30 to 35 MPa (p > 0.1). Scanning electron microscopy (SEM) examinations revealed numerous resin tags, which were similar for the control and the QADM and NAg groups. Adding QADM or NAg markedly reduced the biofilm viability, compared to adhesive control. QADM and NAg together in the adhesive had a much stronger antibacterial effect than using each agent alone (p < 0.05). Adding QADM and NAg in both adhesive and primer had the strongest antibacterial activity, reducing metabolic activity, CFU, and lactic acid by an order of magnitude, compared to control. Significance Without compromising dentin bond strength and resin tag formation, the QADM and NAg containing adhesive and primer achieved strong antibacterial effects against microcosm biofilms for the first time. QADM-NAg adhesive and primer are promising to combat residual bacteria in tooth cavity and invading bacteria at the margins, thereby to inhibit secondary caries. QADM and NAg incorporation may have a wide applicability to other dental bonding systems.

Objectives Secondary caries is the main reason for restoration failure, and replacement of the failed restorations accounts for 50–70% of all restorations. Antibacterial adhesives could inhibit residual bacteria in tooth cavity and invading bacteria along the margins. Calcium (Ca) and phosphate (P) ion release could remineralize the lesions. The objectives of this study were to incorporate nanoparticles of silver (NAg) and nanoparticles of amorphous calcium phosphate (NACP) into adhesive for the first time, and to investigate the effects on dentin bond strength and plaque microcosm biofilms. Methods Scotchbond Multi-Purpose adhesive was used as control. NAg were added into primer and adhesive at 0.1% by mass. NACP were mixed into adhesive at 10%, 20%, 30% and 40%. Microcosm biofilms were grown on disks with primer covering the adhesive on a composite. Biofilm metabolic activity, colony-forming units (CFU) and lactic acid were measured. Results Human dentin shear bond strengths (n=10) ranged from 26 to 34 MPa; adding NAg and NACP into adhesive did not decrease the bond strength (p > 0.1). SEM examination revealed resin tags from well-filled dentinal tubules. Numerous NACP infiltrated into the dentinal tubules. While NACP had little antibacterial effect, NAg in bonding agents greatly reduced the biofilm viability and metabolic activity, compared to the control (p < 0.05). CFU for total microorganisms, total streptococci, and mutans streptococci on bonding agents with NAg were an order of magnitude less than those of the control. Lactic acid production by biofilms for groups containing NAg was 1/4 of that of the control. Significance Dental plaque microcosm biofilm viability and acid production were greatly reduced on bonding agents containing NAg and NACP, without compromising dentin bond strength. The novel method of incorporating dual agents (remineralizing agent NACP and antibacterial agent NAg) may have wide applicability to other dental bonding systems.