Bacterial infection is a serious postoperative complication of joint replacement. To prevent infections related to implantation, we have developed a novel antibacterial coating with Ag-containing hydroxyapatite (Ag-HA). In the present study, we examined the antibacterial activity of Ag-HA implant coatings in the medullary cavity of rat tibiae. Forty 10-week-old rats received implantation of Ag-HA-or HA-coated titanium rods, then were inoculated with $1.0 Â 10 2 colony-forming units of methicillin-resistant Staphylococcus aureus. Bacterial counts were calculated for rats euthanized at 24, 48, and 72 h postoperatively. Serum levels of Ag (in the Ag-HA group only) were calculated for rats euthanized at 24, 48, 72 h and 4 weeks. Radiographic evaluations of bone infection were also performed at 4 weeks. Tibiae from both groups showing infection were evaluated histologically. Significant differences in bacterial counts were seen at 24, 48, and 72 h. Mean concentrations of Ag in serum peaked about 48 h after implantation, then gradually decreased. Mean radiographic scores for infection were significantly lower with Ag-HA implants than with HA implants. Histological examination showed better results for abscesses, bone resorption, and destruction of cortical bone around Ag-HA-coated implants. These results indicate that Ag-HA coatings may help prevent surgical-site infections associated with joint replacement. ß
In recent years, with the rapid advancement and consumerization of virtual reality, augmented reality, mixed reality, and extended reality (XR) technology, the use of XR technology in spine medicine has also become increasingly popular. The rising use of XR technology in spine medicine has also been accelerated by the recent wave of digital transformation (i.e., case-specific three-dimensional medical images and holograms, wearable sensors, video cameras, fifth generation, artificial intelligence, and head-mounted displays), and further accelerated by the COVID-19 pandemic and the increase in minimally invasive spine surgery. The COVID-19 pandemic has a negative impact on society, but positive impacts can also be expected, including the continued spread and adoption of telemedicine services (i.e., tele-education, tele-surgery, tele-rehabilitation) that promote digital transformation. The purpose of this narrative review is to describe the accelerators of XR (VR, AR, MR) technology in spine medicine and then to provide a comprehensive review of the use of XR technology in spine medicine, including surgery, consultation, education, and rehabilitation, as well as to identify its limitations and future perspectives (status quo and quo vadis).
Biofilm-producing bacteria are the principal causes of infections associated with orthopaedic implants. We previously reported that silver-containing hydroxyapatite (Ag-HA) coatings exhibit high antibacterial activity against methicillin-resistant Staphylococcus aureus (MRSA). In the present study, we evaluated the effects of Ag-HA coating of implant surfaces on biofilm formation. Titanium disks (14-mm diameter, 1-mm thickness), one surface of which was coated with HA or 0.5%–3.0% Ag-HA with a thermal spraying technique, were used. In vitro, the disks were inoculated with an MRSA suspension containing 4 × 105 CFU and incubated for 1-2 weeks. In vivo, MRSA-inoculated HA and 3% Ag-HA disks (8.8–10.0 × 108 CFU) were implanted subcutaneously on the back of rats for 1–7 days. All disks were subsequently stained with a biofilm dye and observed under a fluorescence microscope, and biofilm coverage rates (BCRs) were calculated. The BCRs on the Ag-HA coating were significantly lower than those on the HA coating at all time points in vitro (p < 0.05). Similar results were observed in vivo (p < 0.001) without argyria. Ag-HA coating reduced biofilm formation by MRSA in vitro and in vivo; therefore, Ag-HA coating might be effective for reducing implant-associated infections.
Antibacterial silver with hydroxyapatite (Ag-HA) is a promising coating material for imparting antibacterial properties to implants. We previously reported that 3% (w/w) silver with HA (3% Ag-HA) has both antibacterial activity and osteoconductivity. In this study, we investigated the effects of Ag-HA on the in vitro osteoblast function and the in vivo anchorage strength and osteoconductivity of implants. Production of the osteoblast marker alkaline phosphatase, but not cytotoxicity, was observed in cells of the osteoblast cell line MC3T3-E1 cultured on the 3% Ag-HA-coated surface. These results were similar to those observed with silverfree HA coating. In contrast, a significant high level of cytotoxicity was observed when the cells were cultured on a 50% Ag-HA-coated surface. The anchorage strength of implants inserted into the femur of Sprague-Dawley (SD) rats was enhanced by coating the implants with 3% Ag-HA. On the 3% Ag-HA-coated surface, both metaphyseal and diaphyseal areas were largely covered with new bone and had adequate osteoconductivity. These results suggest that 3% Ag-HA, like conventional HA, promotes osteogenesis by supporting osteoblast viability and function and thereby contributes to sufficient anchorage strength of implants. Application of 3% Ag-HA, which combines the osteoconductivity of HA and the antibacterial activity of silver, to prosthetic joints will help prevent postoperative infections. ß
To reduce the incidence of implant-associated infection, we previously developed a novel coating technology using hydroxyapatite (HA) containing silver (Ag). This study examined in vivo acute and subacute toxicity associated with the Ag-HA coating in rat tibiae. Ten-week-old rats received implantation of HA-, 2% Ag-HA-, or 50% Ag-HA-coated titanium rods. Concentrations of silver in serum, brain, liver, kidneys, and spleen were measured in the acute phase (2–4 days after treatment) and subacute phase (4–12 weeks after treatment). Biochemical and histological examinations of those organs were also performed. Mean serum silver concentration peaked in the acute phase and then gradually decreased. Mean silver concentrations in all examined organs from the 2% Ag-HA coating groups showed no significant differences compared with the HA coating group. No significant differences in mean levels of glutamic-oxaloacetic transaminase, glutamic-pyruvic transaminase, lactate dehydrogenase, creatinine, or blood urea nitrogen were seen between the three groups and controls. Histological examinations of all organs revealed no abnormal pathologic findings. No acute or subacute toxicity was seen in vivo for 2% Ag-HA coating or HA coating. Ag-HA coatings on implants may represent biologically safe antibacterial biomaterials and may be of value for reducing surgical-site infections related to implantation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.