The realization of room-temperature processes is an important factor in the development of flexible electronic devices composed of organic materials. In addition, a simple and cost-effective process is essential to produce stable working devices and to enhance the performance of a smart material for flexible, wearable, or stretchable-skin devices. Here, we present a soft friction transfer method for producing aligned polymer films; a glass substrate was mechanically brushed with a velvet fabric and poly(3-hexylthiophene) (P3HT) solution was then spin-coated on the substrate. A P3HT film with a uniaxial orientation was obtained in air at room temperature. The orientation factor was 17 times higher than that of a film prepared using a conventional friction transfer technique at a high temperature of 120 °C. In addition, an oriented film with a thickness of 40 nm was easily picked up and transferred to another substrate. The mechanism for orientation of the film was investigated using six experimental methods and theoretical calculation, and was thereby attributed to a chemical process, i.e., cellulose molecules attach to the substrate and act as a template for molecular alignment.

Vibrational Raman spectra for the C═O stretching modes of three esters with different functional groups (methyl, a single phenyl, and two phenyl groups) were measured in supercritical carbon dioxide (scCO2). The results were compared with Raman spectra for three ketones involving the same functional groups, measured at the same thermodynamic states in scCO2. The peak frequencies of the Raman spectra of these six solute molecules were analyzed by decomposition into the attractive and repulsive energy components, based on the perturbed hard-sphere theory. For all solute molecules, the attractive energy is greater than the repulsive energy. In particular, a significant difference in the attractive energies of the ester-CO2 and ketone-CO2 systems was observed when the methyl group is attached to the ester or ketone. This difference was significantly reduced in the solute systems with a single phenyl group and was completely absent in those with two phenyl groups. The optimized structures among the solutes and CO2 molecules based on quantum chemical calculations indicate that greater attractive energy is obtained for a system where the oxygen atom of the ester is solvated by CO2 molecules.

No abstract