Bioprosthetic heart valve (BPHV) degeneration, characterized by extracellular matrix deterioration, remodeling, and calcification, is an important clinical problem accounting for thousands of surgeries annually. Here we report for the first time, in a series of in vitro accelerated fatigue studies (5-500 million cycles) with glutaraldehyde fixed porcine aortic valve bioprostheses, that the mechanical function of cardiac valve cusps caused progressive damage to the molecular structure of type I collagen as assessed by Fourier transform IR spectroscopy (FTIR). The cyclic fatigue caused a progressive loss of helicity of the bioprosthetic cuspal collagen, which was evident from FTIR spectral changes in the amide I carbonyl stretching region. Furthermore, cardiac valve fatigue in these studies also led to loss of glycosaminoglycans (GAGs) from the cuspal extracellular matrix. The GAG levels in glutaraldehyde crosslinked porcine aortic valve cusps were 65.2 +/- 8.66 microg uronic acid/10 mg of dry weight for control and 7.91 +/- 1.1 microg uronic acid/10 mg of dry weight for 10-300 million cycled cusps. Together, these molecular changes contribute to a significant gradual decrease in cuspal bending strength as documented in a biomechanical bending assay measuring three point deformation. We conclude that fatigue-induced damage to type I collagen and loss of GAGs are major contributing factors to material degeneration in bioprosthetic cardiac valve deterioration.

Elastin, an abundant structural protein present in the arterial wall, is prone to calcification in a number of disease processes including porcine bioprosthetic heart valve calcification and atherosclerosis. The mechanisms of elastin calcification are not completely elucidated. In the present work, we demonstrated calcification of purified elastin in rat subdermal implants (Ca(2+) = 89.73 +/- 9.84 microgram/mg after 21 days versus control, unimplanted Ca(2+) = 0.16 +/- 0.04 microgram/mg). X-ray diffraction analysis along with resolution enhanced FTIR spectroscopy demonstrated the mineral phase to be a poorly crystalline hydroxyapatite. We investigated the time course of calcification, the effect of glutaraldehyde crosslinking on calcification, and mechanisms of inhibition of elastin calcification by pretreatment with aluminum chloride (AlCl(3)). Glutaraldehyde pretreatment did not affect calcification (Ca(2+) = 89.06 +/- 17.93 microgram/mg for glutaraldehyde crosslinked elastin versus Ca(2+) = 89.73 +/- 9.84 microgram/mg for uncrosslinked elastin). This may be explained by radioactive ((3)H) glutaraldehyde studies showing very low reactivity between glutaraldehyde and elastin. Our results further demonstrated that AlCl(3) pretreatment of elastin led to complete inhibition of elastin calcification using 21-day rat subdermal implants, irrespective of glutaraldehyde crosslinking (Ca(2+) = 0.73-2.15 microgram/mg for AlCl(3) pretreated elastin versus 89.73 +/- 9.84 for untreated elastin). The AlCl(3) pretreatment caused irreversible binding of aluminum ions to elastin, as assessed by atomic emission spectroscopy. Moreover, aluminum ion binding altered the spatial configuration of elastin as shown by circular dichroism (CD), Fourier transform infrared (FTIR), and (13)C nuclear magnetic resonance (NMR) spectroscopy studies, suggesting a net structural change including a reduction in the extent of beta sheet structures and an increase in coil-turn conformations. Thus, it is concluded that purified elastin calcifies in rat subdermal implants, and that the AlCl(3)-pretreated elastin completely resists calcification due to irreversible aluminum ion binding and subsequent structural alterations caused by AlCl(3).

Bioprosthetic heart valve (BPHV) degeneration, characterized by extracellular matrix deterioration, remodeling, and calcification, is an important clinical problem accounting for thousands of surgeries annually. Here we report for the first time, in a series of in vitro accelerated fatigue studies (5-500 million cycles) with glutaraldehyde fixed porcine aortic valve bioprostheses, that the mechanical function of cardiac valve cusps caused progressive damage to the molecular structure of type I collagen as assessed by Fourier transform IR spectroscopy (FTIR). The cyclic fatigue caused a progressive loss of helicity of the bioprosthetic cuspal collagen, which was evident from FTIR spectral changes in the amide I carbonyl stretching region. Furthermore, cardiac valve fatigue in these studies also led to loss of glycosaminoglycans (GAGs) from the cuspal extracellular matrix. The GAG levels in glutaraldehyde crosslinked porcine aortic valve cusps were 65.2 ± 8.66 g uronic acid/10 mg of dry weight for control and 7.91 ± 1.1 g uronic acid/10 mg of dry weight for 10-300 million cycled cusps. Together, these molecular changes contribute to a significant gradual decrease in cuspal bending strength as documented in a biomechanical bending assay measuring three point deformation. We conclude that fatigue-induced damage to type I collagen and loss of GAGs are major contributing factors to material degeneration in bioprosthetic cardiac valve deterioration.

Calcification of elastin occurs in many pathological cardiovascular diseases including atherosclerosis. We have previously shown that purified elastin when subdermally implanted in rats undergoes severe calcification and aluminum chloride (AlCl(3)) pretreatment of elastin inhibits calcification. In the present study we investigated whether matrix metalloproteinase (MMP) binding to elastin and elastin degradation is prevented by AlCl(3) pretreatment. Subdermal implantation of AlCl(3)-pretreated elastin showed significantly lower MMP-9 and MMP-2 activity surrounding the implant as compared to the control implants. AlCl(3) pretreatment also significantly inhibited elastin implant calcification at the seven-day implant period (AlCl(3)-pretreated 4.07 +/- 1.27, control 23.82 +/- 2.24 microg/mg; p<0.0001). Moreover, elastin gel zymography studies showed that gel pretreatment with AlCl(3) inhibited elastolysis by MMP-9. We also demonstrate significant suppression of MMP-2 activity in aortic wall segments of AlCl(3)-pretreated porcine bioprosthetic heart valve implants as compared to control valve implants in sheep mitral valve replacement studies. AlCl(3) pretreatment also significantly inhibited calcification of elastin in this model. Thus, we conclude that aluminum ion binding to elastin prevents MMP-mediated elastolysis and thus prevents elastin calcification.

No abstract