Aim To compare (a) enamel carious (EC) and dentin carious (DC) lesions and (b) caries risk, between normal‐weight (NW) and overweight/obese (OW) children/adolescents. Design In this cross‐sectional study, 91 participants aged 6‐12 years were classified according to the body mass index (BMI): NW (n = 50) and OW (n = 41). Caries experience was evaluated using the International Caries Detection and Assessment System (ICDAS) with two thresholds: “EC/DC” (ICDAS 1‐3/4‐6) and “DC” (ICDAS 4‐6). Caries risk was determined by the Caries Management by Risk Assessment (CAMBRA) system. A logistic regression analysis was performed to determine the association among OW, caries thresholds, and caries risk. Results Caries experience was similar for both groups at the “EC/DC” threshold (P = .477) and higher for the NW group at the “DC” threshold (P = .009). For CAMBRA, caries risk classification was similar for both groups (P = .082). The logistic regression showed the OW group was less likely to exhibit radiographically visible proximal carious lesions (odds ratio [OR] of 0.330, P = .019), thick biofilm visible on the tooth surface (OR = 0.360, P = .019), high caries risk (OR = 0.367, P = .039), and moderate‐to‐high caries levels (OR = 0.190, P = .022). Conclusion OW children/adolescents had lower caries experience, at both ICDAS thresholds, and lower caries risk, compared to NW children/adolescents.

Obesity is considered a risk factor for periodontal health due to the low- grade inflammation promoted by the increased adipose tissue. Objective: This study aimed to determine correlations and associations between gingival inflammation (Simplified Oral Hygiene Index, and Gingival Index), salivary immunoglobulin A (s-IgA), and salivary parameters (salivary flow and osmolality) in normal-weight and overweight/obese children. Material and Methods: Ninety-one children, aged 6 to 12 years old (8.6±1.9 years), were divided into two groups according to their body mass index (BMI), circumferences, skinfold measurements and body fat percentage: normal- weight group (NWG; n =50) and overweight/obese group (OG; n =41). A calibrated examiner performed the clinical examination using the Simplified Oral Hygiene Index, Gingival Index, and salivary collection. Data analysis included descriptive statistics and association tests ( p <0.05). Results: OG presented statistically higher s-IgA values compared with NWG, especially among the obese children ( p <0.05). Significant positive correlations between s-IgA and salivary osmolality in OG ( p <0.05), and between s-IgA and BMI values ( p <0.05) and body fat percentage ( p <0.05) were observed among all the children. Effect size varied from moderate for s-IgA values ( d =0.57) to large for BMI ( d =2.60). Conclusion: Gingival inflammation and salivary parameters were similar for NWG and OG; however, s-IgA presented higher values in OG, with correlations between BMI and body fat percentage.

Introdução Os cimentos de ionômero de vidro (CIV) são materiais com baixa resistência à tração e ao cisalhamento, mostrando-se, portanto, contraindicados para áreas sujeitas às grandes cargas oclusais. Objetivo Avaliar o efeito da incorporação de nanotubos de carbono em CIV por meio de dureza superficial Knoop. Material e método Foram confeccionados 48 espécimes, divididos em quatro grupos, de acordo com o tipo de CIV (n=12) – convencional ou de alta viscosidade, incorporados ou não de nanotubos de carbono (NC) a 2%: (A) Vidrion R; (B) Vidrion R + NC 2%; (C) Vitro Molar, e (D) Vitro Molar + NC 2%. Os espécimes foram preparados utilizando-se seringa Centrix, para inserção do material em moldes plásticos, e armazenados em água deionizada por 24 horas. Após polimento, realizou-se o teste de dureza superficial com penetrador do tipo Knoop. Foram realizadas cinco endentações em cada espécime, distanciadas entre si em 100 µm. Resultado Os valores médios de dureza foram 58,96 ± 8,29 (A), 34,81 ± 5,78 (B), 60,84 ± 4,91 (C) e 41,97 ± 5,45 (D). O teste ANOVA detectou diferenças estatisticamente significantes para os dois parâmetros estudados, tipo de material (p=0,016) e inclusão de NC (p<0,0001). Pelo teste de Tukey, observou-se que os grupos A e C foram estatisticamente semelhantes (p>0,05), enquanto os grupos B e D apresentaram diferenças significativas (p<0,05). Ao comparar o fator incorporação ou não de NC, observou-se diferença significativa entre os grupos A e B, e entre os grupos C e D (p<0,05). Conclusão A incorporação de nanotubos de carbono influenciou negativamente os valores de dureza superficial para os dois tipos de CIV utilizados.

Objective: To determine the initial mechanical stabilization of conventional glass ionomer cements (GICs) indicated for the atraumatic restorative treatment (ART) in different storage periods. Material and Methods: Specimens were divided according to the GIC (n=12): IZ -Ion-Z, KM -Ketac Molar Easymix, RS -Riva Self Cure, and GL -Gold Label 9. They were prepared and stored in distilled water. Superficial microhardness (SMH) was evaluated (KHN) in three phases: (A) after 1, (B) 3, and (C) 7 days of storage. Data were submitted to 2-way ANOVA and Tukey tests (α = 5%). Results: The average KHN values for phases A,