Surface-enhanced Raman measurements of <1 μL analyte/colloid meso-droplets on superhydrophobic wires with hydrophilic tips allowed dipicolinic acid, a spore biomarker for Bacillus anthracis (anthrax), to be detected at 10(-6) mol dm(-3). This is equivalent to 18 spores, significantly below the infective dose of 10(4) spores and 2 orders of magnitude better than previous measurements.

Raman analysis of dilute aqueous solutions is normally prevented by their low signal levels. A very general method to increase the concentration to detectable levels is to evaporate droplets of the sample to dryness, creating solid deposits which are then Raman probed. Here, superhydrophobic (SHP) wires with hydrophilic tips have been used as supports for drying droplets, which have the advantage that the residue is automatically deposited at the tip. The SHP wires were readily prepared in minutes using electroless galvanic deposition of Ag onto copper wires followed by modification with a polyfluorothiol (3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluoro-1-decanethiol, HDFT). Cutting the coated wires with a scalpel revealed hydrophilic tips which could support droplets whose maximum size was determined by the wire diameter. Typically, 230 μm wires were used to support 0.6 μL droplets. Evaporation of dilute melamine droplets gave solid deposits which could be observed by scanning electron microscopy (SEM) and Raman spectroscopy. The limit of detection for melamine using a two stage evaporation procedure was 1 × 10(-6) mol dm(-3). The physical appearance of dried droplets of sucrose and glucose showed that the samples retained significant amounts of water, even under high vacuum. Nonetheless, the Raman detection limits of sucrose and glucose were 5 × 10(-4) and 2.5 × 10(-3) mol dm(-3), respectively, which is similar to the sensitivity reported for surface-enhanced Raman spectroscopy (SERS) detection of glucose. It was also possible to quantify the two sugars in mixtures at concentrations which were similar to those found in human blood through multivariate analysis.

Antiferroelectric (Pb,Nb)(Zr,Sn,Ti)O 3 thin films were deposited via a sol-gel process on LaNiO 3-coated silicon substrates. Films showed a strong ͑001͒ preferred orientation upon annealing at 500-700°C for 30 min. The dependence of electrical properties on film thickness has been studied, with the emphasis placed on field-induced phase switching from the antiferroelectric to the ferroelectric state. The decrease of film thickness led to an increase of the phase-switching field along with the appearance of remanent polarization. However, the dielectric constant and maximum polarization decreased with the reduction of film thickness. Saturation polarization was 35 C/cm 2 , which is equal to that observed in bulk samples.