A sepiolite from Vallecas (Spain) was treated with solutions of HC1 (1.25, 2.5, 5.0, 10.0 and 20.0 wt%) at 25°C for 2, 6, 24 and 48 h, respectively. The resulting solids were characterized by XRD, FT-IR and thermal analyses, along with SEM, TEM and nitrogen adsorption isotherms at 77 K. The free silica was digested and determined in all samples. Several samples were seen to have specific surface areas up to 450 m2/g, with a maximum value of 549 m2/g in the sample treated with 1.25 wt% HCl for 48 h. A sudden decrease in specific surface areas was observed when free silica was digested.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.