Surface roughness is extremely important as it influences micro-organism accumulation and consequently oral health. The aim of the present study was to evaluate the influence of mechanical polishing (MP) and chemical polishing (CP) on surface roughness of four heat-cured denture base acrylic resins. Twenty sample discs were prepared for each of the following acrylic resins: Classico (CL), QC 20 (QC), Acron MC (AC) and Onda Cryl (ON). The first two are boiling cured resins and the latter two are microwave cured. After curing and deflasking, samples were ground and subdivided into two groups: MP, which received pumice slurry, chalk powder, soft brush and felt cone, at a bench vice; and CP, which received fluid specifically for chemical polisher. Surface roughness was measured using a Surf Corder SE 1700 rugosimeter. Data collected were statistically analysed by analysis of variance followed by Tukey's test. Surface roughness means in mum were: CL-MP: 0.0350; CL-CP: 0.2298; QC-MP: 0.0307; QC-CP: 0.1792; AC-MP: 0.0312; AC-CP: 0.2700; ON-MP: 0.0321; ON-CP: 0.2949. It can be concluded that MP produced significantly smoother surfaces than CP and that surface roughness because of MP was not influenced by acrylic resin type, whereas this was not true of CP.

The bone anabolic potency of HF loading was overruled by the ALN dosages applied in the present study. Further altering the ALN dosage combined with robust mechanical stimuli needs to be considered in osteoporosis research and eventually therapy.