Abstract:We have studied the dispersion and exfoliation of four inorganic layered compounds, WS 2 , We found that the dispersed concentration of each material falls exponentially with  as predicted by solution thermodynamics. This work shows that solution thermodynamics and specifically solubility parameter analysis can be used as a framework to understand the dispersion of 2-dimensional materials. Finally, we note that in good solvents such as 2 cyclohexylpyrrolidone, the dispersions are temporally stable with >90% of material remaining dispersed after 100 hours. ToC figOver the last decade, 2-dimensional nanomaterials have become one of the most studied subfields of nanoscience. These developments have been spearheaded by research into graphene, a material that is unique due to its combination of thermal, electronic, optical and mechanical properties. 1-5 However, over the last few years, it has become clear that a range of other inorganic layered compounds can be mechanically exfoliated in small quantities to give 2-dimensional nanosheets with interesting properties. 6-10 For example, exfoliated hexagonal boron nitride has been used as a dielectric support in graphene-based transistors 11 while MoS 2 has been fabricated into sensors 10, 12 , transistors 13-15 and integrated circuits. 16 The availability of a wide range of 2-dimensional materials is important as it allows access to a broad palette of physical and chemical properties. A good example is provided by the family of transition metal dichalcogenides (TMDs). These materials have the chemical composition MX 2 where M is a transition metal (commonly, but not limited to Ti, Nb, Ta, Mo, W) and X is a chalcogen (i.e. S, Se, Te). As in graphite, these atoms are covalently bonded into nanosheets which stack into 3-dimensional crystals by van der Waals interactions. These materials are of particular interest because, depending on the combination of metal and chalcogen, the material can be semiconducting or metallic. 17 In addition, the bandgap can vary from a few hundred meV to a few eV, 17 suggesting these materials have potential as versatile electronic device materials.Furthermore, these materials have interesting electrochemical properties which make them suitable for applications such as battery electrodes. 18,19 As with graphene, many applications will require relatively large quantities of material suggesting that a solution processing route is required. 20 A number of possibilities exist. For example, it has been known for many years that materials such as MoS 2 can be exfoliated by 3 lithium intercalation. 21 However, such a route tends to result in structural deformations in some TMDs leading to considerably altered electronic properties. 22 Alternatively, TMDs can be synthesised in the liquid phase. 7,8 Probably the simplest route to liquid exfoliation of layered compounds is sonication assisted exfoliation in solvents [23][24][25][26][27][28][29] or aqueous surfactant solutions. 19,[30][31][32] Here, sonication results in the exfoliation of the ...

No abstract

No abstract

The feasibility of reinforcing conventional carbon fiber composites by grafting carbon nanotubes (CNTs) onto the fiber surface has been investigated. Carbon nanotubes were grown on carbon fibers using the chemical vapor deposition (CVD) method. Iron was selected as the catalyst and predeposited using the incipient wetness technique before the growth reaction. The morphology of the products was characterized using scanning electron microscopy (SEM), which showed evidence of a uniform coating of CNTs on the fiber surface. Contact angle measurements on individual fibers, before and after the CNT growth, demonstrated a change in wettability that can be linked to a change of the polarity of the modified surface. Model composites based on CNT-grafted carbon fibers/epoxy were fabricated in order to examine apparent interfacial shear strength (IFSS). A dramatic improvement in IFSS over carbon fiber/epoxy composites was observed in the single fiber pull-out tests, but no significant change was shown in the push-out tests. The different IFSS results were provisionally attributed to a change of failure mechanism between the two types of tests, supported by fractographic analysis.