Broad-band organic photomultiplication-type photodetectors were successfully fabricated with one photon harvesting layer and one photomultiplication layer, exhibiting broad response range from 300 to 1000 nm and over 50400% EQE at 360 nm.

Broadband photomultiplication type all-polymer photodetectors (PM-APDs) are achieved on the basis of ITO/PFN-Br/PBDB-T:PYF-T-o (3:100, wt/wt)/LiF/Au as the configuration. Amounts of isolated hole traps are formed with PBDB-T encircled by PYF-T-o...

Photomultiplication type organic photodetectors (PM-OPDs) have attracted enormous interests owing to the high sensitivity on weak light, especially for excellent parasitic stability with single-polymer as active layers. Herein, three kinds...

The emerging polymerized small-molecule acceptors (PSMAs) with near-infrared (NIR) absorption have not only significantly boosted the power conversion efficiencies (PCEs) of all-polymer solar cells (all-PSCs) but have also exhibited great potential for sensitive NIR polymeric photodetectors (PPDs). However, there is no report regarding PSMAs with photo-response that can approach 1000 nm, which is an important criterion for applications in NIR-responsive all-PSCs and PPDs. Herein, by unidirectionally inserting vinylene segments into a selenophene-rich polymer backbone to improve the electron-donating strength and quinoidal character, an asymmetric PSMA, namely, PY3Se-1V, was developed, which showed an extensively red-shifted absorption approaching 1000 nm. The PBDB-T:PY3Se-1V-based binary all-PSCs achieve a decent PCE of 13.2% and a record-high photocurrent density of 25.9 mA cm −2 due to the significantly broadened photo-response and efficient photon-to-electron conversion. More encouragingly, narrowband photomultiplication (PM)-type PPDs based on poly(3-hexylthiophene-2,5-diyl) (P3HT):PY3Se-1V were developed, delivering an exceptionally high external quantum efficiency of 3680% and a responsivity of 28 A W −1 at an NIR peak of 960 nm under −50 V bias, which is reported for the first time in PM-type PPDs with a response approaching 1000 nm.

Broadband photomultiplication-type organic photodetectors (PM-OPDs) were prepared with PMBBDT:PY3Se-2V (1:1, wt/wt) as the absorbing layer (AL) and PC 71 BM:P3HT (100:5, wt/wt) as the photomultiplication layer (PML) on the basis of the sandwich structure. The incident photons from ultraviolet light to the near-infrared region can be harvested by AL. The rather less P3HT in PML can produce plenty of isolated hole traps with P3HT surrounded by PC 71 BM; the electron tunneling injection induced by trapped holes near the Ag electrode can lead to the photomultiplication (PM) phenomenon. The performance of PM-OPDs can be effectively improved by optimizing the AL thickness. The optimal PM-OPDs exhibit a broad spectral response from 300 to 1050 nm as well as an external quantum efficiency (EQE) of 5800% at 340 nm at 10 V bias, along with a specific detectivity (D*) of 3.78 × 10 13 Jones. The spectral response of PM-OPDs is controlled by the trapped-hole distribution near the Ag electrode, primarily originating from the photogenerated holes in AL. To further optimize the spectral response of PM-OPDs, the optical filter layer (OFL) was used to manipulate light field distribution in AL. The violet, red, and near-infraredlight PM-OPDs were developed by employing different OFLs.