This research explores the correlation between the structural properties of supramolecular biocomposites and their mechanical strength. Hybrid biocomposites composed of surface-modified hydroxyapatite nano-particles and supramolecular polycaprolactone (SP PCL), were prepared at different compositions, and their mechanical, thermal and viscoelastic properties as well as biodegradability, biocompatibility and cytotoxicity were evaluated in vitro. The results were compared with those for SP PCL/naked hydroxyapatite nano-composites. We show that surface modification of hydroxyapatite nanoparticles resulted in outstanding improvement of tensile strength and modulus up to 3.6 and 2.2-fold, respectively. At above 10 wt% HAp and 20 wt% HApUPy, heterogeneous nano-composites with inferior mechanical properties were obtained. Based on rheological (in steady shear mode) and small/wide angle X-ray scattering measurements, unusual improved mechanical properties were ascribed to the formation of supramolecular clusters around nanoparticles. In-vitro degradation of the supramolecular nano-composites was also studied to investigate the overall product biodegradation as well as toxicity of the degradation product(s).

The porous structures of Si-HA and Al2O3 were synthesized using the replication technique. The compressive strength of porous bioceramics increased with increasing Al2O3 content up to 30 wt% (ANOVA, P<.05).

Arms bearing ureido-pyrimidinone functional groups with self-association capability (through quadruple hydrogen bonds) were successfully grafted onto hydroxyapatite nanoparticles. The supramolecularly modified nanoparticles (nHApUPy) exhibited enhanced colloidal stability compared to the original hydroxyapatite nanoparticles and were uniformly dispersed in supramolecular polycaprolactone in PCL(UPy)2/HApUPy nanocomposites at different filler loadings. The combined atomic force microscopy, mechanical, and rheological analyses confirmed a high degree of compatibility of HApUPy nanoparticles with the polymer matrix. The temperature dependence of the supramolecular structure in PCL(UPy)2/HApUPy nanocomposites was determined from dynamic rheological measurements at two different temperatures, 60°C and 85°C. The osteocompatibility of the nanocomposite containing HApUPy nanoparticles was compared to the pure polymer. The preliminary cell results clearly confirm that the supramolecular nanocomposites are nontoxic and biocompatible. Therefore, it is postulated that supramolecular nanocomposites provide a new way of tuning the mechanical properties of the supramolecular polymers, particularly supramolecular polycaprolactones.