In this article four samples of HgBa2Ca2Cu2.4Ag0.6O8+δ were prepared and irradiated with different doses of gamma radiation 6, 8 and 10 Mrad. The effects of gamma irradiation on structure of HgBa2Ca2Cu2.4Ag0.6O8+δ samples were characterized using X-ray diffraction. It was concluded that there effect on structure by gamma irradiation. Scherrer, crystallization, and Williamson equations were applied based on the X-ray diffraction diagram and for all gamma doses, to calculate crystal size, strain, and degree of crystallinity. It is observed through the results that gamma irradiation causes a change in the atomic density, crystal size, strain, degree of crystallinity and thus a change in the diffraction angle and intensity peaks. It was found that the highest crystal size was 69.3269 nm at 4MRad dose, crystallization is 69.3269 at 4MRad and the strain is 0.0068 when sample without radiation.

In this manuscript, the effect of substituting strontium with barium on the structural properties of Tl0.8Ni0.2Sr2-xBrxCa2Cu3O9-δ compound with x= 0, 0.2, 0.4, have been studied. Samples were prepared using solid state reaction technique, suitable oxides alternatives of Pb2O3, CaO, BaO and CuO with 99.99% purity as raw materials and then mixed. They were prepared in the form of discs with a diameter of 1.5 cm and a thickness of (0.2-0.3) cm under pressures 7 tons / cm2, and the samples were sintered at a constant temperature of 860 ° C. The structural properties were studied using X-ray diffraction for all samples, and the results showed that the samples have tetragonal structure and the change of the parameters structure with the change of the barium concentration. Full Width Half Maximum (FWHM) was calculated by Orange Pro using X-RAY data. The crystal size was calculated using Scherrer and Willeamson-Heall methods, where the results showed that the crystal size, compliance and degree of crystallinity changed with the change of barium concentration, and the highest average for the crystal size was 70.0271nm at x=0, and crystallization at 61.46% at x=0.6, and the strain decreased to 0.0037 when barium concentration equals 0.4.