This paper studied the efficiency of electrocoagulation/electroflotation in removing colour from real textile wastewater by using aluminum and iron electrodes in an innovative pilot external-loop airlift reactor of 150 L. The reactor was designed to operate in batch and continuous modes. The real effluent contained 90% of disperse dye and 10% of reactive dye. A complete flotation of pollutants with acceptable mixing was achieved in this reactor using only the overall liquid recirculation induced by H 2 microbubbles. The treatment of these discharges was easier using electrodes of iron rather than aluminum. The optimal initial pH was 10 for both aluminum and iron electrodes. By using iron electrodes, the maximum decolourisation efficiency and COD reduction efficiency reached respectively 96% and 65% for 90 minutes of treatment. Similarly, by using aluminum electrodes, the maximum decolourisation efficiency reached 90%, COD reduction reached 51% for 120 minutes of treatment. In the case of an initial pH slightly different to 10, the required time to reach 90% ranged from double to triple.

No abstract

The inhibitory activity of the expired egg-white carbon steel (CS) extract in HCl solution was studied in this article. The extract was examined using FT-IR, and the surface was examined using a scanning electron microscope (SEM) and energy-dispersive X-ray analysis (EDX). Weight loss techniques at various temperatures were used to examine corrosion investigations (298, 308, 318, and 328 K), concentrations (100, 200, 400, and 800 mg. L−1) of extracts, and electrochemical measurements (potentiodynamic polarization (PDP) and impedance spectroscopy (EIS) at 25°C and different concentrations. Results. Results obtained through EIS demonstrated a maximal inhibition efficiency of 90% at an inhibitor concentration of 800 mg. L−1. Moreover, the findings of the potentiodynamic polarization indicated that egg-white extract was a mixed type of inhibitor and slowed down both cathodic and anodic reactions. For weight loss analysis, an inhibitory potency (89, 83, 77, and 71%) at various temperatures (298, 308, 318, and 328 K) was demonstrated, respectively. It indicates that the temperature rise contributes to a decrease in the resistance of the carbon steel. The adsorption of the expired egg-white extract was spontaneous with physisorption and chemisorption according to the Langmuir isotherm model, according to adsorption isotherm studies.

No abstract

No abstract