No abstract

Plant-mediated green synthesis of nanomaterials has been increasingly gaining popularity due to its eco-friendly nature and cost-effectiveness. In the present study, we synthesized silver nanoparticles (AgNPs) by using an aqueous solution of Saudi Origanum vulgare L. plant extract as a bioreducing agent. The as-synthesized AgNPs were characterized using various microscopic and spectroscopic techniques. The results indicated the formation of crystalline face-centered cubic (fcc) AgNPs. Additionally, FT-IR study confirmed that the O. vulgare L. extract not only functioned as a bioreductant but also stabilized the surface of the AgNPs by acting as a capping agent. Moreover, the effect of the amount of the plant extract on the size and the antimicrobial activity of the NPs was also assessed. It was found that with increasing amounts of plant extract, the size of the NPs was decreased. Moreover, as-synthesized AgNPs as well as O. vulgare L. plant extract were separately tested to examine their antimicrobial activities. The activities were tested against various bacterial and fungal microorganisms including Shigella sonnei, Micrococcus luteus, Escherichia coli, Aspergillus flavus, Alternaria alternate, Paecilomyces variotii, Phialophora alba, and so on. These results evidently show that the inclusion of O. vulgare L. extracts improves the solubility of AgNPs, which led to a significant enhancement in the toxicity of the NPs against the assessed microorganisms.

In the light of a recent study which identiÐed the beneÐcial inÑuence of poorly crystallised ferrihydrite on the activity of CO conversion catalysts comprising gold nanoparticles on oxidic iron, we Fe 5 HO 8 É 4H 2 O have investigated three series of ferrihydrite-rich samples prepared by coprecipitation. The samples were structurally and chemically characterised using X-ray di †raction and both 57Fe and 197Au Mo ssbauer spectroscopy, and tested for CO oxidation at room temperature using a microreactor with on-line GC. The highest activity, 100% conversion after 20 min on line, was observed in a dried sample that contained ferrihydrite and a non-crystalline and possibly hydrated gold oxyhydroxide phase, The AuOOH É xH 2 O. activity of the same materials after calcination, where the gold was transformed to 3È5 nm Au metal particles and the ferrihydrite to hematite, was less than ca. 7%. This is the Ðrst report of a synergistic interaction between and ferrihydrite resulting in an active catalyst for room temperature CO oxidation, AuOOH É xH 2 O and contrasts with previous work which has been interpreted in terms of the requirement for metallic Au nanoparticles.

No abstract

The first imidazole-type carbene complex of platinum(II), cis-(C2H4)(1-ethyl-3-methylimidazol-2-ylidene)PtCl2, has been obtained by reacting PtCl2 and PtCl4 with ethylene in the basic [EMIM]Cl/AlCl3 (1.3:1) ionic liquid (where [EMIM]+ = 1-ethyl-3-methylimidazolium) at 200 degrees C and structurally characterized (monoclinic P21/c space group, a = 10.416(2) A, b = 7.3421(9) A, c = 15.613(2) A, beta = 101.53(2) degrees, Z = 4). This complex can be regarded as a stable analogue of the pi-alkene-Pd(II)-carbene intermediate in the Heck reaction. In addition, a series of new N,N'-dialkylimidazolium salts of platinum group metals of the type [RMIM]2[MCln], where [RMIM+] = 1-alkyl-3-methylimidazolium and M = Pt(II), Pt(IV), or Ir(IV), have been prepared and characterized. The salts [EMIM]2[PtCl6] (1) and [EMIM]2[PtCl4] (2) were prepared in the ionic liquid [EMIM]Cl/AlCl3 and the salts [BMIM]2[PtCl4] (3) and [BMIM]2[PtCl6] (4) (where [BMIM]+ = 1-n-butyl-3-methylimidazolium) and [EMIM]2-[IrCl6] (5) in aqueous or acetonitrile media. From TGA measurements, salts 1-5 decompose in air in several steps eventually to form the corresponding metal, the onset of decomposition being observed at (degree C) 260 (1), 220 (2), 200 (3), 215 (4), and 210 (5). The structures of 1, 2, and 5 were determined by single-crystal X-ray analysis. The three salts crystallize in the monoclinic P21/n space group (1, a = 7.6433(9) A, b = 16.353(2) A, c = 9.213(1) A, beta = 113.56(1) degrees, Z = 2; 2, a = 8.601(1) A, b = 8.095(2) A, c = 13.977(2) A, beta = 91.75(2) degrees, Z = 2; 5, a = 10.353(2) A, b = 9.759(2) A, c = 10.371(2) A, beta = 92.98(3) degrees, Z = 2).