Coating is one of the most effective measures to protect metallic materials from corrosion. Various types of coatings such as metallic, ceramic and polymer coatings have been investigated in a quest to find durable coatings to resist electrochemical decay of metals in industrial applications. Many polymeric composite coatings have proved to be resistant against aggressive environments. Two major applications of ferrous materials are in marine environments and in the oil and gas industry. Knowing the corroding behavior of ferrous-based materials during exposure to these aggressive applications, an effort has been made to protect the material by using polymeric and ceramic-based coatings reinforced with nano materials. Uncoated and coated cast iron pipeline material was investigated during corrosion resistance by employing EIS (electrochemical impedance spectroscopy) and electrochemical DC corrosion testing using the “three electrode system”. Cast iron pipeline samples were coated with Polyvinyl Alcohol/Polyaniline/FLG (Few Layers Graphene) and TiO2/GO (graphene oxide) nanocomposite by dip-coating. The EIS data indicated better capacitance and higher impedance values for coated samples compared with the bare metal, depicting enhanced corrosion resistance against seawater and “produce water” of a crude oil sample from a local oil rig; Tafel scans confirmed a significant decrease in corrosion rate of coated samples.

ZnO/GO (Graphene Oxide) and SAN (Styrene Acrylonitrile)/PANI (Polyaniline)/FLG (Few Layers Graphene) nanocomposite coatings were produced by solution casting and sol-gel methods, respectively, to enhance corrosion resistance of ferrous based materials. Corrosive seawater and ‘produced crude oil water’ environments were selected as electrolytes for this study. Impedance and coating capacitance values obtained from Electrochemical Impedance Spectroscopy (EIS) Alternating Current (AC technique) showed enhanced corrosion resistance of nanocomposites coatings in the corrosive environments. Tafel scan Direct Current (DC technique) was used to find the corrosion rate of nanocomposite coating. SAN/PANI/FLG coating reduced the corrosion of bare metal up to 90% in seawater whereas ZnO/GO suppressed the corrosion up to 75% having the impedance value of 100 Ω. In produced water of crude oil, SAN/PANI/FLG reduced the corrosion up to 95% while ZnO/GO suppressed the corrosion up to 10%. Hybrid composites of SAN/PANI/FLG coatings have demonstrated better performances compared to ZnO/GO in the corrosive environments under investigation. This study provides fabrication of state-of-the-art novel anti corrosive nanocomposite coatings for a wide range of industrial applications. Reduced corrosion will result in increased service lifetime, durability and reliability of components and system and will in turn lead to significant cost savings.

The dye sensitized solar cells technology is one of the highly efficient, low cost and easily fabricated renewable energy technology. The highly soluble PVAc was prepared by solution polymerization. The PVAc was employed as an electrolyte in third generation, Dye sensitized solar cell (DSSC). The PVAc was characterized using SEM, XRD and conductivity measuring techniques. The prepared electrolyte behaved as gel electrolyte. SEM images shows the excellent dispersion PVAc in liquid electrolyte. The conversion efficiency achieved using gel electrolyte was 4.18%, which was comparable to liquid electrolyte with a value of 4.57%. This new technique reduces the degradation of DSCs rising from volatilization and leakage of the liquid electrolyte and endorses the commercialization process of DSSC.