The aim of this study was to investigate the effect of elastane linear density and draft ratio on the physical and mechanical properties of core-spun yarns. Twenty yarn samples were prepared on industrial scale in a spinning mill with two different yarn linear densities, each with different two elastane deniers and five draft ratios. It was found that core-spun yarn's tenacity, elongation and hairiness are affected not only by the overall yarn linear density but also by the elastane linear density and the draft ratio. However, the effect of elastane linear density and draft ratio was not found to be statistically significant on the yarn mass variations and total imperfections, which are only affected by the overall yarn liner density. A statistically significant interaction for yarn elongation at break was found between the yarn liner density and the elastane linear density concluding that elastane linear density used in the core must be compatible with the overall yarn liner density for attaining the best yarn elongation.
Elastane percentage in the core-spun cotton yarn of a specific linear density can be affected in two ways: either by changing the elastane denier or the draft ratio. The purpose of this study was to find out whether different mechanical properties of fabrics woven from such yarns simply depend upon the elastane percentage or whether the method of achieving a desired elastane percentage has specific effects. It was found through regression analyses that both the elastane denier and the draft ratio are almost equally important for fabric tear strength and stretchability, whereas the fabric tensile strength is predominantly influenced by the elastane denier while the fabric recovery after stretch is mainly influenced by the elastane draft ratio.
Herein, the hydrophobic and self-cleaning properties of three different fabric surfaces have been evaluated after applying titanium dioxide (TiO 2 ) nanofinishes. The nanoparticles were prepared by sol-gel techniques and were characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and dynamic light scattering (DLS) methods. The ultra-refined particles were applied over three different fabric substrates having similar weave of Z-twill (3/1). The yarns of 100% polyester, blend of viscose with mod-acrylic and high performance polyethylene containing 16 yarn count (Ne) and 31.496 and 15.748 ends/cm and picks/cm, respectively, were used for required fabric preparation. The different fabric structures were applied with self-cleaning finish of TiO 2 nanoparticles prepared in our laboratory and the results were compared with commercially available finish Rucoguard AFR. The static contact angles, UV-protection factor, air permeability and hydrophobic activity of nanofinished fabric helped in evaluating their breathability and self-cleaning properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.