Poly(epsilon-caprolactone) (PCL) microspheres containing c. 3% bovine serum albumin (BSA) were prepared by melt encapsulation and solvent evaporation techniques. PCL, because of its low Tm, enabled the melt encapsulation of BSA at 75 degrees C thereby avoiding potentially toxic organic solvents such as dichloromethane (DCM). Unlike the solvent evaporation method, melt encapsulation led to 100% incorporation efficiency which is a key factor in the microencapsulation of water-soluble drugs. Examination of the stability of the encapsulated protein by sodium dodecyl sulphate-polyacrylamide gel electrophoresis (SDS-PAGE) demonstrated that protein integrity was unaffected by both methods of encapsulation. In vitro release of the protein into phosphate buffer examined at 37 degrees C from microspheres prepared by both techniques showed that the release rate from melt-encapsulated microspheres was somewhat slower compared to the release from solvent-evaporated spheres. Both released around 20% of the incorporated protein in 2 weeks amounting to approximately 6.5 micrograms mg-1 of microspheres. Although the diffusivity of macromolecules in PCL is rather low, it is shown that PCL microspheres are capable of delivering sufficient quantity of proteins by diffusion for prolonged periods to function as a carrier for many vaccines. Unlike poly(lactic acid) (PLA) and poly(glycolic acid) (PGA) polymers which generate extreme acid environments during their degradation, the delayed degradation characteristics of PCL do not generate an acid environment during protein release and, therefore, may be advantageous for sustained delivery of proteins and polypeptides.

No abstract

No abstract

Oxidation of trichloroethylene and derivatives of phenol, which are toxic compounds present in water, to harmless species has been carried out in the presence of modified clays such as HDTMA-immobilized-interlayerMn(VII) (surfactant immobilized manganate clay) and M n+ -bent-Mn (VII) (metal cations like Al, Cr, Fe, Cu, Ni, Mn & Zn impregnated on manganate clays), by treating the toxic compounds with HDTMA-immobilized-interlayer-Mn(VII) clay and M n+ -bent-Mn (VII) clays. The oxidation reaction was monitored by measuring the absorbance after every hour using a UV-Visible spectrophotometer at a definite wavelength.

The liquid phase esterification of phenyl acetic acid with p-cresol over different metal cation exchanged montmorillonite nanoclays yields p-cresyl phenyl acetate. Different metal cation exchanged montmorillonite nanoclays (Mn+ = Al3+, Zn2+, Mn2+, Fe3+, Cu2+) were prepared and the catalytic activity was studied. The esterification reaction was conducted by varying molar ratio of the reactants, reaction time and catalyst amount on the yield of the ester. Among the different metal cation exchanged catalysts used, Al3+-montmorillonite nanoclay was found to be more active. The characterization of the material used was studied under different techniques, namely X-ray diffraction, scanning electron microscopy and thermogravimetric analysis. The product obtained, p-cresyl phenyl acetate, was identified by thin-layer chromotography and confirmed by Fourier transform infrared, 1H NMR and 13C NMR. The regeneration activity of used catalyst was also investigated up to fourth generation.