We have synthesized, characterized, and computationally simulated/validated the behavior of two new metal-organic framework (MOF) materials displaying the highest experimental Brunauer-Emmett-Teller (BET) surface areas of any porous materials reported to date (~7000 m(2)/g). Key to evacuating the initially solvent-filled materials without pore collapse, and thereby accessing the ultrahigh areas, is the use of a supercritical CO(2) activation technique. Additionally, we demonstrate computationally that by shifting from phenyl groups to "space efficient" acetylene moieties as linker expansion units, the hypothetical maximum surface area for a MOF material is substantially greater than previously envisioned (~14600 m(2)/g (or greater) versus ~10500 m(2)/g).

Given that energy (exciton) migration in natural photosynthesis primarily occurs in highly ordered porphyrin-like pigments (chlorophylls), equally highly ordered porphyrin-based metal-organic frameworks (MOFs) might be expected to exhibit similar behavior, thereby facilitating antenna-like light-harvesting and positioning such materials for use in solar energy conversion schemes. Herein, we report the first example of directional, long-distance energy migration within a MOF. Two MOFs, namely F-MOF and DA-MOF that are composed of two Zn(II) porphyrin struts [5,15-dipyridyl-10,20-bis(pentafluorophenyl)porphinato]zinc(II) and [5,15-bis[4-(pyridyl)ethynyl]-10,20-diphenylporphinato]zinc(II), respectively, were investigated. From fluorescence quenching experiments and theoretical calculations, we find that the photogenerated exciton migrates over a net distance of up to ~45 porphyrin struts within its lifetime in DA-MOF (but only ~3 in F-MOF), with a high anisotropy along a specific direction. The remarkably efficient exciton migration in DA-MOF is attributed to enhanced π-conjugation through the addition of two acetylene moieties in the porphyrin molecule, which leads to greater Q-band absorption intensity and much faster exciton-hopping (energy transfer between adjacent porphyrin struts). The long distance and directional energy migration in DA-MOF suggests promising applications of this compound or related compounds in solar energy conversion schemes as an efficient light-harvesting and energy-transport component.

HKUST-1, a metal-organic framework (MOF) material containing Cu(II)-paddlewheel-type nodes and 1,3,5-benzenetricarboxylate struts, features accessible Cu(II) sites to which solvent or other desired molecules can be intentionally coordinated. As part of a broader investigation of ionic conductivity in MOFs, we unexpectedly observed substantial proton conductivity with the "as synthesized" version of this material following sorption of methanol. Although HKUST-1 is neutral, coordinated water molecules are rendered sufficiently acidic by Cu(II) to contribute protons to pore-filling methanol molecules and thereby enhance the alternating-current conductivity. At ambient temperature, the chemical identities of the node-coordinated and pore-filling molecules can be independently varied, thus enabling the proton conductivity to be reversibly modulated. The proton conductivity of HKUST-1 was observed to increase by ~75-fold, for example, when node-coordinated acetonitrile molecules were replaced by water molecules. In contrast, the conductivity became almost immeasurably small when methanol was replaced by hexane as the pore-filling solvent.

Open coordination sites (OCSs) in metal-organic frameworks (MOFs) often function as key factors in the potential applications of MOFs, such as gas separation, gas sorption, and catalysis. For these applications, the activation process to remove the solvent molecules coordinated at the OCSs is an essential step that must be performed prior to use of the MOFs. To date, the thermal method performed by applying heat and vacuum has been the only method for such activation. In this report, we demonstrate that methylene chloride (MC) itself can perform the activation role: this process can serve as an alternative "chemical route" for the activation that does not require applying heat. To the best of our knowledge, no previous study has demonstrated this function of MC, although MC has been popularly used in the pretreatment step prior to the thermal activation process. On the basis of a Raman study, we propose a plausible mechanism for the chemical activation, in which the function of MC is possibly due to its coordination with the Cu(2+) center and subsequent spontaneous decoordination. Using HKUST-1 film, we further demonstrate that this chemical activation route is highly suitable for activating large-area MOF films.