Soda residue (SR), a waste by-product of sodium carbonate production, occupies land resources and pollutes the environment seriously. To promote the resource reusing of waste SR, this paper studies the feasibility of utilizing SR for the preparation of soda residue soil (SRS) through laboratory and field tests. The SR and fly ash (FA) were mixed with six different proportions (SR:FA is 1:0, 10:1, 8:1, 6:1, 3:1, 1:1) to prepare SRS, and the optimum water content, maximum dry density, shear strength, and unconfined compression strength of the SRS were measured. The representative SRS (SR:FA is 10:1) was selected to investigate the compression performance and collapsibility. The preparation and filling method of SRS in the field was proposed, and the effects of gravel, sand, and lime on the mechanical properties of SRS were studied through field tests. The results show that the addition of FA contributed to the strength development of SR, and the addition of lime, sand and rubble have a significant effect on the subgrade bearing capacity of SRS. The subgrade bearing capacity and deformation modulus of SRS in field tests is more than 210 kPa and 34.48 MPa, respectively. The results provide experimental basis and reference for the preparation of SRS, the scientific application of SRS in geotechnical engineering to promote sustainable development.

Based on the vertical compressive static load test and pile mechanics test of three large diameter bored piles (one of the test piles was treated with postgrouting) in granite gneisses foundation, the bearing capacity, deformation characteristics, and influencing factors of the single pile under the limit state are analyzed and compared with the recommended values of survey report and the recommended values of current codes. By comparing the measured and theoretical values of pile axial force, the bearing capacity of cast-in-place pile under normal and limit conditions is analyzed. The experimental results show that the Q-s curve of large-diameter rock-socketed mud wall retaining bored pile with a length-diameter ratio of 25–33 and rock-socketed depth of 5–8 d shows a rapid growth. After grouting treatment, the ultimate compressive bearing capacity of single pile is improved, the maximum settlement is reduced by 6.6%, the rebound rate is reduced by 11.1%, and the settlement effect of controlling pile top is not significant. The bearing capacity and deformation characteristics of the three test piles are less affected by length-diameter ratio and rock-socketed depth. For postgrouting piles, the ratio of frictional resistance of rock-socketed segment and the ratio of pile lateral resistance are less affected by length-diameter ratio and rock-socketed depth, while, for postgrouting piles, the ratio of pile lateral resistance is more affected by rock-socketed depth. The pile end resistance ratio of the three test piles is significantly affected by the rock-socketed depth, whether or not the pile side postgrouting treatment is carried out.

As part of a large converter project in Shandong Province, vertical static load tests and internal force tests were conducted on three large-diameter rock-socketed piles, their load transfer mechanism was clarified, and the ultimate side resistance and ultimate resistance performance characteristics of the rock-socketed sections were analyzed. The test results showed that the three test piles were damaged under maximum loading, the Q-s curve exhibited a steep drop, the pile compression was around 1.2 times the pile diameter, and the bearing capacity of a single pile did not meet the design requirements. The side and end resistances of the three test piles all reached their ultimate values, but the ultimate side resistance was lower than the lower limit of the recommended value in the current technical code for building pile foundations. The end resistance under maximum loading accounted for 38.4–53.8% of the peak load, which was relatively high. By comparing it with other studies, there was no significant correlation between the coefficient of rock ultimate side resistance of the rock-socketed segment and the pile diameter of the rock-socketed segment. However, the coefficient of ultimate resistance increased gradually with the pile diameter. However, the latter correlation was not significant when the pile diameter was less than 1000 mm.