The production, composition, wear resistance and corrosion resistance of thermal diffusion zinc coatings produced at JSC PNTZ are considered. Specially treated zinc powders with nanocrystallized oxide on the surface of the particles are used in production. The process is capable to provide unique composition and microstructure of coatings. The results of laboratory and field tests show excellent characteristics of coatings in conditions typical for the oil industry.

The accumulated research data of tubing fragments after operation made it possible to generalize and systematize information on the prevailing type of corrosion damage and operating conditions that determine the mechanism of their development. Understanding basic laws of the development of corrosion processes in specific operating conditions, allows to select the optimal type of tubing for these conditions more accurately.

High-strength oil country tubular goods (OCTG) like C110, according to standard API 5CT (yield strength at least 758 MPa), are subject to requirements in terms of mechanical and corrosion properties. In this work, we studied the microstructure of seamless casing tubes made of class C110 high-strength steel with a 194.5 mm diameter and 19.7 mm wall thickness, and its influence on sulfide stress corrosion cracking (SSC). Casing tubes were obtained from continuous billets by screw piercing with preliminary quenching and tempering. It was shown that cracking during the tests always begins from the inner surface of the tube. Rough segregation bands were found on the inner tube surface, which occupies about a third of the thickness of the wall. To increase the resistance of 0.3C-Cr-Mn-Mo + 0.15(V + Nb + Ti) steel to SSC, primary recommendations for adjusting the chemical composition, production technology and heat treatment were developed.

High-strength oil country tubular goods (OCTG) like C110, according to standard API 5CT (yield strength at least 758 MPa), are subject to requirements in terms of mechanical and corrosion properties. In this work, we studied the influence of seamless tubes microstructure with a 177.8 mm diameter and 10.36 mm wall thickness of class С110 high-strength steel to sulfide stress corrosion cracking (SSC) and sulfide stress corrosion cracking with low strain rates (SSRT). Tubes were obtained from continuous billets by screw piercing with preliminary quenching and tempering. It was established that cracking during the tests always begins from the inner surface of the tube. Rough segregation bands were found on the inner tube surface, which occupies about a third of the thickness. It is shown that the SSRT assessment technique allows to estimate the threshold value of the resistance.