A novel material preparation method is presented that facilitates accurate measurement of the degree of cure and resin content within carbon fibre reinforced polymer composites (CFRPs). When using conventional specimen preparation for standard thermal analysis, it is demonstrated that the experimentally-obtained enthalpy

Discontinuous fibre reinforced composites enable the manufacture of integrated structural components via the complex flow process of compression moulding. However, such processes can lead to the formation of detrimental weld-lines. Here, the meso-structure of carbon fibre sheet moulding compounds (C-SMC) was analysed using conventional non-destructive techniques and automated eddy current (EC) scanning, as well as destructive methods, in an attempt to identify defects such as weld-lines in this class of materials. Compression-moulded plaques with forced weld-lines in two different configurations (adjacent and opposing flow joints) were analysed, showing up to 80% strength reduction versus a defect-free plaque. The EC-determined local fibre orientation and elucidated local microstructure matched those obtained using conventional techniques, showing a dramatic fibre tow alignment parallel to the weld-lines. It was found that failure occurred in proximity to the “non-uniformity” defect regions identified by EC analyses, demonstrating the use of robot-guided EC for successful defect detection in C-SMC structures.