Two-step thermochemical cycling was achieved using CeO2 with sub-micrometer sized macropores, allowing for substantially improved CO production at fast cycle rates when compared to nonporous CeO2. The effects of porosity, pore order, and packing density were probed by synthesizing ceria materials with different morphologies. Polymeric colloidal spheres were used as templates for the synthesis of three-dimensionally ordered macroporous (3DOM) CeO2 and nonordered macroporous (NOM) CeO2. Aggregated CeO2 nanoparticles with feature sizes similar to those in 3DOM CeO2 were prepared by fragmenting 3DOM CeO2 into its building blocks using ultrasonication. The three templated materials and nonporous, commercial CeO2 were tested in thermochemical cycles using an infrared furnace. CeO2 was reduced at ∼1200 °C, and the reduced CeO2−δ materials were reoxidized under CO2 at ∼850 °C. The high temperatures required for cycling induced changes in the morphology of the porous materials, which were characterized by electron microscopy, X-ray diffraction, and nitrogen sorption measurements. In spite of sintering, the macroporous materials retained an interconnected pore network during 55 cycles, providing a 10-fold enhancement in CO productivity and production rate when compared to nonporous CeO2. Additionally, 3DOM CeO2 provided the fastest rate of CO production of all tested materials and also retained the smallest solid feature sizes. This boost in reaction kinetics allowed for extremely rapid cycling with less than a minute required for complete reduction or oxidation. Characterization of the porous materials also provided some insight into thermal gradients that developed in the sample bed as a result of rapid heating and cooling.

The mechanisms driving microstructure formation in template-confined Pechini-type gel systems involving solid solutions of cerium oxide with alkaline earth metals are investigated. Three-dimensionally ordered macroporous microspheres and more extended bicontinuous networks with hierarchical porosity are synthesized directly from a Pechini sol–gel precursor within a colloidal crystal template. The type of morphology generated is related to the mechanisms of phase separation in the precursor, namely, nucleation and growth vs spinodal decomposition. These mechanisms are, in turn, determined by the citric acid concentration in the initial precursor solution and by electrostatic interactions of the precursor with the polymeric template. Microspheres generated by the nucleation-and-growth pathway can be produced between 1–3 μm in size, with polydispersities below 15%. They retain the ordered porous network left by removal of the template. The number of nucleation sites (i.e., oligomers and longer chains of complexed metal) is dependent on the reactant imbalance between metal–citrate complexes and ethylene glycol, as predicted by step-growth polymerization statistics. This method expands existing phase-separation techniques currently exploited in metal alkoxide systems to the production of microstructure in ceramic oxides.

A low-coordinate iron hydride complex bearing an unsymmetrical NpN (enamido-phosphinimine) ligand scaffold was synthesized and fully characterized. Insertion reactivity with azobenzene, 3-hexyne, and 1-azidoadamantane was explored, and the isolated products were analogous to previously reported β-diketiminate iron hydride insertion products. Surprisingly, the NpN iron hydride displays unprecedented reactivity toward hexafluorobenzene, affording an NpN iron fluoride complex and pentafluorobenzene as products. The NpN iron hydride is a precatalyst for catalytic hydro-defluorination of perfluorinated aromatics in the presence of silane. Kinetic studies indicated that the rate-determining step during catalysis involved silane.

Poly(methylhydrosiloxane) (PMHS) has been examined for its ability to reduce and subsequently cyclize carbohydrate substrates using catalytic tris(pentafluorophenyl)borane (BCF).

In an effort to mimic N-diaryl-β-diketiminate ligands (Nacnac), we have converted N-arylimine phosphine ligands to enamine-phosphinimines via the Staudinger reaction. By varying the aryl azide, one can access enamine-phosphinimine ligands with the same or different N-aryl substituents on both the enamine and phosphinimine units, which allows this intrinsically unsymmetrical bidentate donor set to present variable steric effects at the metal center. The enamine-phosphinimine was deprotonated and used in metathetical reactions with Fe(ii) bromide precursors to generate low coordinate complexes of the empirical formula [(CY5)NpN(Ar,Ar')]FeBr (where CY5 = cyclopentenyl; Ar,Ar' = 2,6-diisopropylphenyl, 2,6-dimethylphenyl, 2,4,6-trimethylphenyl). Depending on the substituents, these bromide derivatives can be monomeric or dimeric via bromide bridges. Reduction under dinitrogen using potassium graphite generates the dinitrogen complexes ([(CY5)NpN(Ar,Ar')]Fe)2(μ-N2) for Ar,Ar' = 2,6-diisopropylphenyl, and Ar = 2,6-dimethylphenyl, Ar' = 2,4,6-trimethylphenyl. However, for the former, a unsymmetrical side product can be isolated that has a bridging N-2,6-diisopropylphenylimide unit with one enamido-phosphine ligand bound to one iron and the other iron stabilized with an intact enamido-phosphinimine. When the steric bulk is reduced on both nitrogen donors, a complicated product mixture is obtained after reduction from which a small amount of [(CY5)NpN(Ar,Ar')]Fe[(CY5)NP(Ar)] (Ar,Ar' = 2,6-dimethylphenyl) could be isolated. All of these complexes are paramagnetic and have been characterized by elemental analysis, magnetic studies and X-ray crystallography.