This paper investigates the effect of the ratio of ammonium nitrate (AN) on the structural, microstructural, magnetic, and alternating current (AC) conductivity properties of barium hexaferrite (BaFe12O19). The BaFe12O19 were prepared by using the salt melt method. The samples were synthesized using different powder-to-salt weight ratio variations (1:3, 1:4, 1:5, 1:6 and 1:7) of BaCO3 + Fe2O3 and ammonium nitrate salt. The NH4NO3 was melted on a hot plate at 170 °C. A mixture of BaCO3 and Fe2O3 were added into the NH4NO3 melt solution and stirred for several hours using a magnetic stirrer under a controlled temperature of 170 °C. The heating temperature was then increased up to 260 °C for 24 hr to produce an ash powder. The x-ray diffraction (XRD) results show the intense peak of BaFe12O19 for all the samples and the presence of a small amount of the impurity Fe2O3 in the samples, at a ratio of 1:5 and 1:6. From the Fourier transform infra-red (FTIR) spectra, the band appears at 542.71 cm−1 and 432.48 cm−1, which corresponding to metal–oxygen bending and the vibration of the octahedral sites of BaFe12O19. The field emission scanning electron microscope (FESEM) images show that the grains of the samples appear to stick each other and agglomerate at different masses throughout the image with the grain size 5.26, 5.88, 6.14, 6.22, and 6.18 µm for the ratios 1:3, 1:4, 1:5, 1:6, and 1:7 respectively. From the vibrating sample magnetometer (VSM) analysis, the magnetic properties of the sample ratio at 1:3 show the highest value of coercivity Hc of 1317 Oe, a saturation magnetization Ms of 91 emu/g, and a remnant Mr of 44 emu/g, respectively. As the temperature rises, the AC conductivity is increases with an increase in frequency.

Synthesis of nanocrystalline strontium ferrite (SrFe12O19) via sol–gel is sensitive to its modification parameters. Therefore, in this study, an attempt of regulating the pH as a sol–gel modification parameter during preparation of SrFe12O19 nanoparticles sintered at a low sintering temperature of 900 °C has been presented. The relationship of varying pH (pH 0 to 8) on structural, microstructures, and magnetic behaviors of SrFe12O19 nanoparticles were characterized by X-ray diffraction (XRD), field emission scanning microscope (FESEM), and vibrating sample magnetometer (VSM). Varying the pH of precursor exhibited a strong effect on the sintered density, crystal structure and magnetic properties of the SrFe12O19 nanoparticles. As the pH is 0, the SrFe12O19 produced relatively largest density, saturation magnetization, Ms, and coercivity, Hc, at a low sintering temperature of 900 °C. The grain size of SrFe12O19 is obtained in the range of 73.6 to 133.3 nm. The porosity of the sample affected the density and the magnetic properties of the SrFe12O19 ferrite. It is suggested that the low-temperature sintered SrFe12O19 at pH 0 displayed Ms of 44.19 emu/g and Hc of 6403.6 Oe, possessing a significant potential for applying in low-temperature co-fired ceramic permanent magnet.