In this study, we examined the effect of the transmitted amount of visible light through a resin composite on the curing depth and polymerization conversion. Transmitted amount of visible light was strongly dependent on the magnitude of refractive index difference that existed between the resin and silica filler. More specifically, the differences arose from the type of base monomer used. The transmitted amount of visible light exhibited a good correlation with the curing depth and Knoop hardness ratio of the bottom surface against the top surface of the resin composite. To improve the polymerization conversion of the cavity floor, it is important to reduce the refractive index difference that exists between the base resin and silica filler.

No abstract

Water is required to ionize acid resin monomers for demineralization of tooth substrates. We tested the null hypothesis that altering the water concentration in two-step self-etching primers has no effect on their aggressiveness and bonding efficacy to dentin. Five experimental self-etching primers were prepared with resin-water-ethanol volume ratios of 9-0-1, 8-1-1, 7-2-1, 5-4-1, and 3-6-1. They were applied to smear-layer-covered dentin, followed by a bonding resin and composite build-ups for microtensile bond testing and TEM examination of tracer penetration. Increasing water concentration from 0-60 vol% improved acidic monomer ionization that was manifested as increasing hybrid layer thickness. However, significantly higher bond strength was observed in the 7-2-1 group, with minimal nanoleakage in the corresponding hybrid layer. When self-etching primers are formulated, a balance must be achieved to provide sufficient water for adequate ionization of the acidic monomers, without lowering the resin concentration too much, to optimize their bonding efficacy to dentin.