Objectives: To investigate the effects of a coffee beverage and two whitening systems on the surface roughness and gloss of glazed Lithium Disilicate Glass-Ceramics (LDGC) for computer-aided design/computer-aided manufacturing (CAD/CAM) systems. Methods: Sixty-eight LDGC disks (12 × 10 × 2 mm) were prepared from blocks of CAD/CAM systems (IPS e.max CAD ceramic). Baseline measurements for surface roughness (Ra) and gloss (GU) were taken using a 3-D optical profilometer and a glossmeter, respectively; then specimens were randomized into four groups ( n = 17). All specimens were immersed in a coffee solution (24 h × 12 days) then subjected to two whitening systems. G1-negative control (kept moist × 7 days); G2-positive control (brushed with distilled water, 200 g/load, 2 min twice daily × 7 days); G3-whitening toothpaste (Colgate optic white; relative dentin abrasivity (RDA) = 100, 200 g/load, 2 min twice daily × 7 days); and G4-simulated at-home bleaching protocol (Opalescence,15% carbamide peroxide (CP), 6 h/day × 7 days). The study outcomes were measured at baseline and after the treatments. Data were analyzed using paired T-test and one-way ANOVA (α = 0.05). Results: The mean surface roughness significantly increased ( p ⩽ 0.002) for all groups after the designated treatment protocols. Among groups, the mean surface roughness of G2 and G3 were significantly higher ( p ⩽ 0.001) (Ra: 0.51 and 0.57 μm, respectively) compared to the control group (Ra: 0.23 μm), and were not significantly different from G4 (Ra: 0.46 μm). Surface gloss decreased with no significant change within or among groups after treatment. Conclusion: All glazed LDGC had a significant increase in surface roughness after being subjected to simulated 1 year of coffee drinking and whitening systems (15% CP and whitening toothpaste), and the greatest change was associated with brushing (simulating 8 months). However, coffee beverages and whitening systems had no significant effect on the surface gloss.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.