An effort was carried out to fully utilise fast-growing Acacia hybrid usage in the timber engineering field; however, the research data are still lacking. This paper aims to evaluate the physical and mechanical properties performance between untreated (control) and treated with 10% copper chrome arsenic of Acacia hybrid collected from Daikin Plantation Sdn. Bhd. Bintulu, Sarawak at air-dry condition at different age groups using the small clear method. Mechanical properties test refers to shear parallel to grain (tangential and radial directions), cleavage (tangential and radial directions), and tension parallel to grain test. Meanwhile, the physical properties test refers to moisture content (MC) and density test. After treatment, mechanical properties increase with an average of 13.67%; meanwhile, moisture content decreased with an average of 0.58% or 0.09% MC, and density slightly increased with an average of 0.44% or 0.002 g/cm3. Results indicate that 10-year-old Acacia hybrid exhibits the highest strength values in shear parallel to the grain, tension parallel to the grain, and cleavage, followed by 13-year-old and 7-year-old. Treated samples in the tangential direction performed better with consistent mean results than that of the untreated samples, while radial direction gave a high average strength increment when treated.

The slow growth rate of primer species has affected the supply available to accommodate the market demand. To overcome these problems, a study was carried out to fully utilise fast-growing timber as the primary resource to ensure the demand for timber logs continues. This paper aimed to determine mechanical strength properties, treatability retention, and hazard classification of 7-, 10- and 13-year-old small-clear samples of Acacia mangium superbulk collected from Daiken Plantation Sdn. Bhd. Bintulu, Sarawak, following treatment with 10% copper chrome arsenic. As a result of this study, the maximum strength was obtained from the 10-year-old age group, with the modulus of rupture (MOR), the modulus of elasticity (MOE), and compression parallel to the grain values of small-clear treated Acacia mangium superbulk reaching 118.76 N/mm2, 15,020 N/mm2, and 57.82 N/mm2, respectively. In addition, the treatability retentions obtained were 149.27 L/m3, 147.25 L/m3, and 141.09 L/m3, which were recorded from the 7-, 10-, and 13-year-old samples, respectively. Meanwhile, the dry-salt retentions obtained from the 7-, 10- and 13-year-old samples were 14.93 kg/m3, 14.73 kg/m3, and 14.11 kg/m3, respectively. Hence, this species is classified as moderately difficult to treat under CCA (treatability retention: 80–160 L/m3) and is categorised under the hazard class of H4 (dry salt retention: 12–16 kg/m3).