Kallikrein (PKa), generated by activation of its precursor prekallikrein (PK), plays a role in the contact activation phase of coagulation and functions in the kallikrein-kinin system to generate bradykinin. The general dogma has been that the contribution of PKa to the coagulation cascade is dependent on its action on FXII. Recently this dogma has been challenged by studies in human plasma showing thrombin generation due to PKa activity on FIX and also by murine studies showing formation of FIXa-antithrombin complexes in FXI deficient mice. In this study, we demonstrate high-affinity binding interactions between PK(a) and FIX(a) using surface plasmon resonance and show that these interactions are likely to occur under physiological conditions. Furthermore, we directly demonstrate dose- and time-dependent cleavage of FIX by PKa in a purified system by sodium dodecyl sulfate-polyacrylamide gel electrophoresis analysis and chromogenic assays. By using normal pooled plasma and a range of coagulation factor-deficient plasmas, we show that this action of PKa on FIX not only results in thrombin generation, but also promotes fibrin formation in the absence of FXII or FXI. Comparison of the kinetics of either FXIa- or PKa-induced activation of FIX suggest that PKa could be a significant physiological activator of FIX. Our data indicate that the coagulation cascade needs to be redefined to indicate that PKa can directly activate FIX. The circumstances that drive PKa substrate specificity remain to be determined.

Hip resurfacing with cobalt-chromium (CoCr) alloy was developed as a surgical alternative to total hip replacement. However, the biological effects of nanoparticles generated by wear at the metal-on-metal articulating surfaces has limited the success of such implants. The aim of this study was to investigate the effects of the combined exposure to CoCr nanoparticles and cobalt ions released from a resurfacing implant on monocytes (U937 cells) and whether these resulted in morphology changes, proliferation alterations, toxicity and cytokine release. The interaction between prior exposure to Co ions and the cellular response to nanoparticulate debris was determined to simulate the situation in patients with metal-on-metal implants receiving a second implant. Effects on U937 cells were mainly seen after 120h of treatment. Prior exposure to Co ions increased the toxic effects induced by the debris, and by Co ions themselves, suggesting the potential for interaction in vivo. Increased TNF-α secretion by resting cells exposed to nanoparticles could contribute to osteolysis processes in vivo, while increased IFN-γ production by activated cells could represent cellular protection against tissue damage. Data suggest that interactions between Co ions and CoCr nanoparticles would occur in vivo, and could threaten the survival of a CoCr metal implant.

Adverse tissue responses to prostheses wear particles and released ions are important contributors to hip implant failure. In implant-related adverse reactions T-lymphocytes play a prominent role in sustaining the chronic inflammatory response. To further understand the involvement of lymphocytes in metal-on-metal (MoM) implant failure, primary human lymphocytes were isolated and treated with cobalt-chromium (Co-Cr) wear debris and Co ions, individually, and in combination, for 24, 48 and 120 h. There was a significant increase in cell number where debris was present, as measured by the Neutral Red assay. Interleukin-6 (IL-6), interferon-γ (IFN-γ) and tumour necrosis factor-α (TNF-α) secretion levels significantly decreased in the presence of metal particles, as measured by ELISA. Interleukin-2 (IL-2) secretion levels were significantly decreased by both debris and Co ions. Flow cytometry analysis showed that the metal nanoparticles induced a significant increase in apoptosis after 48-h exposure. This investigation showed that prolonged exposure (120 h) to metal debris induces lymphocyte proliferation, suggesting that activation of resting lymphocytes may have occurred. Although cytokine production was affected mainly by metal debris, cobalt toxicity may also modulate IL-2 secretion, and even Co ion concentrations below the MHRA guideline levels (7 ppb) may contribute to the impairment of immune regulation in vivo in patients with MoM implants.

Joint replacement has proven to be an extremely successful and cost-effective means of relieving arthritic pain and improving quality of life for recipients. Wear debris-induced osteolysis is, however, a major limitation and causes orthopaedic implant aseptic loosening, and various cell types including macrophages, monocytes, osteoblasts, and osteoclasts, are involved. During the last few years, there has been increasing concern about metal-on-metal (MoM) hip replacements regarding adverse reactions to metal debris associated with the MoM articulation. Even though MoM-bearing technology was initially aimed to extend the durability of hip replacements and to reduce the requirement for revision, they have been reported to release at least three times more cobalt and chromium ions than metal-on-polyethylene (MoP) hip replacements. As a result, the toxicity of metal particles and ions produced by bearing surfaces, both locally in the periprosthetic space and systemically, became a concern. Several investigations have been carried out to understand the mechanisms responsible for the adverse response to metal wear debris. This OPEN ACCESSLubricants 2015, 3 540 review aims at summarising in vitro analyses of the toxicity, immunological, and gene expression effects of cobalt ions and wear debris derived from MoM hip implants.