Alloy 617 OCC, a variant of INCONEL 617 with optimised chemical composition, has been produced in India for manufacture of superheater and reheater tubing in boilers operating in advanced ultrasupercritical (A-USC) power plants. The tubing encounters intense hot corrosion conditions during service. The present study deals with hot corrosion behaviour of 617 OCC in A-USC environment. The environment occurring in A-USC plants was simulated in the laboratory by exposing the material coated with a mixture of salts at 700°C in a flowing gas mixture. For use in A-USC boiler technology, the metal loss due to fireside corrosion of the material should be less than 2 mm in 200,000 hours. The loss obtained in the present study was nearly 5 times this value. The corrosion processes were studied using SEM/EDAX, XRD and thermogravimetry. The degradation mechanisms coming into play, disqualifying the material for use in A-USC plants, would be discussed.