In order to avoid the negative effect of contamination of composite resins with powdered latex gloves on the bond strength of two-step self-etching adhesive systems, the use of unpowdered latex gloves is recommended with these adhesive systems. SUMMARYThe aim of the present study was to evaluate the effect of composite resin contamination with powdered and unpowdered latex gloves on the shear bond strength of etch-and-rinse and two-step self-etch adhesive systems. Standard flat dentin surfaces were prepared on the facial aspect of 120 bovine incisors and randomly assigned into two (n=60) groups: group 1: Single Bond (SB), group 2: Clearfil SE Bond (CSE). Furthermore, each group was randomly subdivided into three (n=20) based on the type of composite contamination (without contamination, contamination with powdered latex gloves, and contamination with unpowdered latex gloves). The adhesives were applied and resin composite bonded to the dentin. After thermocycling, the specimens were subjected to a shear bond strength test. Two-way analysis of variance (ANOVA) and a post hoc Bonferroni test were used for statistical analysis. One-way ANOVA was used to compare shear bond strength values in each group. Statistical

Bur-prepared cavities represented less interfacial gap width than laser-prepared cavities. A self-etching adhesive system showed the least interfacial gap compared to etch-and-rinse adhesives and performed similarly in bur-and laser-prepared cavities. SUMMARYOne of the challenges in durability of posterior tooth-colored restorative materials is polymerization shrinkage, which results in gap formation between the restoration and tooth structure. The aim of the present study was to investigate marginal adaptation of Class II composite restorations using a self-etching and two etch-and-rinse adhesive systems in cavities prepared either with bur or Er,-Cr:YSGG laser. A total of 45 extracted sound human premolars were selected. In each tooth, mesial and distal Class II cavities were prepared either by a diamond bur or by Er,-Cr:YSGG laser with the margins 1 mm apical to the cemento-enamel junction. Then the teeth were randomly divided into three groups of 15 each, according to the type of the adhesive system used (Single Bond, Single Bond 2, Parnian Alizadeh Oskoee, DDS, MS, associate professor,

SUMMARY This study aimed to evaluate the effect of toothbrushing on enamel surface roughness at three different intervals after daily bleaching treatment. Eighty enamel slabs were initially evaluated for surface roughness and then randomly divided into four groups. The bleaching procedure was carried out for 21 days, six hours daily. In the control group (group 1), the specimens were not brushed after bleaching, but in groups 2–4, they were brushed with toothpaste immediately, one hour, or two hours after bleaching, respectively. Then the specimens were stored in artificial saliva. Enamel surface roughness was reevaluated at the end of the period. Kruskal-Wallis and Mann-Whitney U tests showed statistically significant differences in the means of surface roughness values between the immediately brushed group and the three other groups (p<0.001). Daily toothbrushing immediately after bleaching increased enamel surface roughness; however, postponing the procedure for one or two hours after daily bleaching and exposing the specimens to artificial saliva during the study period resulted in enamel surface roughness comparable to that of the control group.