The effects of Ba-doping on the structure and photocatalytic performance of GaOOH were investigated for the first time. Compared with pure GaOOH, when GaOOH with different Ba content was used, the removal rate of enrofloxacin was increased by more than 20% in 60 min.

BiSnSbO6 with strong photocatalytic activity was first fabricated by a high-temperature, solid-state sintering method. The resulting BiSnSbO6 was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), UV-vis diffuse reflectance spectroscopy (DRS) and X-ray photoelectron spectroscopy (XPS). The results showed that BiSnSbO6, with a pyrochlore structure and a cubic crystal system by a space group Fd3m, was well crystallized. The lattice parameter or the band gap of BiSnSbO6 was 10.234594 Å or 2.83 eV. Compared with N-doped TiO2, BiSnSbO6 showed higher photocatalytic activity in the degradation of benzotriazole and rhodamine B. The apparent first-order rate constant for BiSnSbO6 in the degradation of benzotriazole and rhodamine B was 0.0182 min−1 and 0.0147 min−1, respectively. On the basis of the scavenger experiment, during the photocatalytic process, the main active species were arranged in order of increasing photodegradation rate: •OH < •O2− < h+. The removal rate of benzotriazole or rhodamine B was approximately estimated to be 100% with BiSnSbO6 as a photocatalyst after 200 min visible-light irradiation. Plentiful CO2 produced by the experiment indicated that benzotriazole or rhodamine B was continuously mineralized during the photocatalytic process. Finally, the possible photodegradation pathways of benzotriazole and rhodamine B were deduced.

A GaOOH/ZnBiNbO5 composite was constructed by loading dispersed GaOOH rods on the surface of ZnBiNbO5 particles and characterizations, including SEM-EDS, XRD, FT-IR spectroscopy, XPS, and UV-Vis DRS were performed.