No abstract

The various solutions tested did not have any deleterious effects on the Co-Cr alloy surface. Steradent, however, presented the smallest ionic release.

Purpose To compare the effect of solutions of effervescent tablets (ET), cetylpyridinium chloride (CPC), and experimental solutions of Ricinus communis on the surface of cobalt‐chromium (Co‐Cr) alloys. Materials and Methods Fifty‐five specimens of Co‐Cr were prepared by the lost‐wax casting method using circular patterns (∅12 × 3 mm). The specimens were randomly divided into 5 groups: deionized water (control); 2% R. communis; 10% R. communis; ET, and CPC. The surface roughness of specimens (n = 10) was evaluated before immersion (baseline), and at simulated times of ½, 1, 2, 3, 4, and 5 years, by laser confocal microscope (Sa, μm) and profilometer (Ra, μm). The surface topography and chemical composition (n = 1) was qualitatively analyzed with scanning electron microscopy (SEM), and energy dispersive X‐ray spectrometry (EDS). Data were subjected to Kruskal–Wallis followed by Dunn tests, and Friedman followed by Wilcoxon tests (α = 0.05). Results For Sa, there was no difference for the solution factor. For the time factor a significant difference was found with 2% R. communis solution among baseline and ½, 2, 3, and 5 years (p < 0.001) and with 10% R. communis solution between 1 and 2 years (p = 0.007), with decreasing roughness over time. For Ra, cetylpyridinium chloride exhibited less roughness than 10% R. communis solution in ½ (p = 0.048) and 5 years (p = 0.013). In the SEM and EDS analysis the solutions did not present deleterious effects or changes in the chemical composition on the surfaces. Conclusions Although a significant difference was found for the roughness, the results, below 0.2 μm, are clinically acceptable. Thus, all solutions can be used safely in removable partial denture cleaning for a period of 5 years.

The aim of this study was to evaluate the effect of cleaning solutions on the retention force of o-ring-type overdenture attachments. The effect of four solutions on nitrile rings were evaluated: Cepacol (C), Cepacol with fluoride (CF), Listerine (L) and 0.05% sodium hypochlorite (SH); deionized water (DW) was used as a control. Matrices containing two implants and abutments and acrylic specimens with the metal capsules were obtained and divided into the groups. A simulation of 90 overnight immersions (8 h) was performed, and the tensile strength value was obtained at the beginning (T0) and in every 30 days (T1, T2 and T3) (n=6). In order to analyze o-ring surface damage after the immersions, a scanning electron microscopy (SEM) was used (n=1). For statistical analysis of the results, analysis of variance (ANOVA) and multiple comparisons with Bonferroni adjustment (test power=1.000; a=0.05) were used. There was a significant difference for the factors time (p<0.001), solution (p<0.001) and for the interaction time × solution (p<0.001). Considering the times of each solution, only for DW there was no significant loss of retention over time. Comparing the solutions in each moment, there was no difference among the solutions in T0. From T1, CF and SH provided less retention than DW (p<0.005). Through SEM it was possible to observe changes in the surface of the CF and SH nitrile o-rings. CF and SH should be avoided due to deleterious action in o-rings.

No abstract