Thin-film photovoltaic devices based on chalcopyrite Cu(In,Ga)Se2 (CIGS) absorber layers show excellent light-to-power conversion efficiencies exceeding 20%. This high performance level requires a small amount of alkaline metals incorporated into the CIGS layer, naturally provided by soda lime glass substrates used for processing of champion devices. The use of flexible substrates requires distinct incorporation of the alkaline metals, and so far mainly Na was believed to be the most favourable element, whereas other alkaline metals have resulted in significantly inferior device performance. Here we present a new sequential post-deposition treatment of the CIGS layer with sodium and potassium fluoride that enables fabrication of flexible photovoltaic devices with a remarkable conversion efficiency due to modified interface properties and mitigation of optical losses in the CdS buffer layer. The described treatment leads to a significant depletion of Cu and Ga concentrations in the CIGS near-surface region and enables a significant thickness reduction of the CdS buffer layer without the commonly observed losses in photovoltaic parameters. Ion exchange processes, well known in other research areas, are proposed as underlying mechanisms responsible for the changes in chemical composition of the deposited CIGS layer and interface properties of the heterojunction.

Thin film solar cells with a Cu(In,Ga)Se2 (CIGS) absorber layer achieved efficiencies above 20%. In order to achieve such high performance the absorber layer of the device has to be doped with alkaline material. One possibility to incorporate alkaline material is a post deposition treatment (PDT), where a thin layer of NaF and/or KF is deposited onto the completely grown CIGS layer. In this paper we discuss the effects of PDT with different alkaline elements (Na and K) on the electronic properties of CIGS solar cells. We demonstrate that whereas Na is more effective in increasing the hole concentration in CIGS, K significantly improves the pn-junction quality. The beneficial role of K in improving the PV performance is attributed to reduced recombination at the CdS/CIGS interface, as revealed by temperature dependent J-V measurements, due to a stronger electronically inverted CIGS surface region. Computer simulations with the software SCAPS are used to verify this model. Furthermore, we show that PDT with either KF or NaF has also a distinct influence on other electronic properties of the device such as the position of the N1 signal in admittance spectroscopy and the roll-over of the J-V curve at low temperature. In view of the presented results we conclude that a model based on a secondary diode at the CIGS/Mo interface can best explain these features.

Direct and inverse photoemission were used to study the impact of alkali fluoride postdeposition treatments on the chemical and electronic surface structure of Cu(In,Ga)Se2 (CIGSe) thin films used for high-efficiency flexible solar cells. We find a large surface band gap (E(g)(Surf), up to 2.52 eV) for a NaF/KF-postdeposition treated (PDT) absorber significantly increases compared to the CIGSe bulk band gap and to the Eg(Surf) of 1.61 eV found for an absorber treated with NaF only. Both the valence band maximum (VBM) and the conduction band minimum shift away from the Fermi level. Depth-dependent photoemission measurements reveal that the VBM decreases with increasing surface sensitivity for both samples; this effect is more pronounced for the NaF/KF-PDT CIGSe sample. The observed electronic structure changes can be linked to the recent breakthroughs in CIGSe device efficiencies.

The introduction of a KF post-deposition treatment (KF PDT) of Cu(In,Ga)Se 2 (CIGS) thin films has led to the achievement of several consecutive new world record efficiencies up to 21.7% for the CIGS solar cell technology. The beneficial effect of the KF PDT on the photovoltaic parameters was observed by several groups in spite of differing growth methods of the CIGS layer. For CIGS evaporated at lower temperature on alkali-free, flexible plastic substrates, a postdeposition treatment to add Na was already successfully applied. However with the introduction of additional KF under comparable conditions, distinctly different influences on the final absorber alkali content as well as surface properties are observed. In this work we discuss in more details the intrinsically different role of both alkali-treatments by combining several microstructural and compositional analysis methods. The ion exchange of Na by K in the bulk of the absorber is carefully analyzed, and further evidences for the formation of a K-containing layer on the CIGS surface with increased surface reactivity are given. These results shall serve as a basis for the further understanding of the effects of alkali PDT on CIGS and help identifying research needs to achieve even higher efficiencies.