This article reports the synthesis and characterization of pure and N-, B-, and Ag-doped TiO 2 and the ability of these oxides to photodegrade methylene blue (MB) under sunlight or UV-ABC radiation. The compounds were synthesized using the sol-gel method and characterized by scanning electron microscopy, X-ray diffraction, diffuse reflectance spectroscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis, and X-ray photoelectron spectroscopy. Photocatalytic efficiency was significantly increased by N-doping, resulting in 98% MB decomposition under UV-ABC irradiation for 180 min. Ag-and B-doped TiO 2 lowered MB degradation rates to 52 and 73%, respectively, compared with pure TiO 2 . The same behavior was observed with exposure to UV-Vis, with 88, 65, 60, and 42% MB removal with N-doped, pure, B-doped, and Ag-doped TiO 2 , respectively. Under visible light alone, N-doped TiO 2 exhibited higher photocatalytic efficiency than commercial P25-type TiO 2 . Photocatalysis with N-doped TiO 2 proved to be a promising alternative for MB degradation, given the potential of employing solar energy, thus minimizing operating costs.

This paper reports the synthesis, characterization, and application of TiO2 and TiO2/Ag nanoparticles for use in photocatalysis, employing the herbicide methylviologen (MV) as a substrate for photocatalytic activity testing. At suitable metal to oxide ratios, increases in silver surface coating on TiO2 enhanced the efficiency of heterogeneous photocatalysis by increasing the electron transfer constant. The sol-gel method was used for TiO2 synthesis. P25 TiO2 was the control material. Both oxides were subjected to the same silver incorporation process. The materials were characterized by conventional spectroscopy, SEM micrography, X-ray diffraction, calculation of surface area per mass of catalyst, and thermogravimetry. Also, electron transfers between TiO2 or TiO2/Ag and MV in the absence and presence of sodium formate were investigated using laser flash photolysis. Oxides synthesized with 2.0 % silver exhibited superior photocatalytic activity for MV degradation.