The type of acrylic resin (base or reline) had no significant effect on the viability of cells. Vinegar and chlorhexidine digluconate solutions increased in cytotoxic effect over time, and were strongly cytotoxic after 6 months of immersion. Sodium perborate and sodium hypochlorite were noncytotoxic in all periods of time tested.
In the case of heat-polymerized resins, the level of residual monomer decreases with the increasing curing time and increases with decreasing temperature [3,6]. With respect to the curing cycles, it has been found that resins with rapid cycle releases higher levels of residual monomer [6]. Moreover, Jorge et al. [7] reported that long cycle acrylic resin Lucitone 550 reduced the number of vi-
AbstractObjective: The purpose of this study was to evaluate the effectiveness of complementary heat treatment and water storage in reducing cytotoxicity of acrylic resins denture bases used in Brazil by the MTT assay.Material and Methods: First, nine specimens were fabricated from metal matrix in the form of discs with 14 mm in diameter and 1.2 mm of thick. Immediately after making, 24 or 48 hours after storage in distilled water, the samples of heat-polymerized resins were divided into 3 groups (n = 3) according to the type of thermal treatment: Group 1: samples were individually exposed to microwave energy (500 W for 3 minutes); Group 2: samples were immersed in water at 55 0 C for 60 minutes; Group 3: samples did not receive heat treatment. To prepare the extracts, 3 samples of each group were placed into vials containing 3 mL of culture medium and stored at 37°C for 24 hours. L929 cells were used and the MTT assay was performed to analyze the cellular metabolism. Two-factor analysis of variance was used to detect significant among groups at 5% significance.Results: After statistical analysis, the materials were classified according to the cytotoxic effect: non-cytotoxic, slightly cytotoxic; moderately cytotoxic; and strongly cytotoxic. The results showed that the resins ranged from moderately cytotoxic to non-cytotoxic, but no statistically significant difference among experimental groups. Furthermore, the water storage and thermal treatments reduced the cytotoxicity of the resins.
Conclusions:It was concluded that the resins studied are potentially toxic and that treatments can decrease their cytotoxicity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.