The spontaneous adsorption of organic molecules on a variety of planar and nonplanar substrates, that is, self assembly, can generate films just one molecule thick. These nanoscale, self-assembled monolayer (SAM) films have been extensively used to engineer surfaces with well-defined properties. Their utility has been demonstrated in a wide range of applications, including wetting, adhesion, lubrication, patterning, and molecular recognition. Many SAM systems have been investigated, but alkanethiols adsorbed on gold are the most successful combination. This pairing offers a variety of advantages, including the ability to tune precisely the interfacial properties of a surface through the well-established organic synthetic methodologies that have been developed for preparing custom ω-terminated alkanethiols. Alkanethiolate monolayers are moderately stable at room temperature; however, these films degrade over time and readily desorb upon moderate heating. This shortcoming limits the use of SAMs in applications involving elevated temperatures or harsh environments. Accordingly, new adsorbates with multiple bonding moieties have been created to enhance the stability and versatility of SAMs. In this Account, we examine a variety of multidentate adsorbate structures that have been used to generate SAMs on planar substrates and on nanoparticles. Each of these chelating adsorbates (bidentates and tridentates) has been designed to generate well-defined organic monolayer films with multiple attachment points to the underlying substrate. This bonding arrangement allows the formation of SAMs with enhanced stability through the entropy-driven "chelate effect". The research examined here demonstrates that multidentate adsorbates provide robust films: they enable the use of SAMs under conditions that are incompatible with SAMs derived from normal alkanethiols. Another advantage offered by multidentate adsorbates is the capacity for new paradigms in thin-film composition. In particular, appropriately designed chelating adsorbates can be engineered to have two or more chemically distinct terminal groups that are covalently linked to the same underlying headgroup, without adding steric bulk that might prove detrimental to the resultant assembly. This strategy allows the generation of homogeneously mixed multicomponent surfaces, overcoming the problem of phase separation or "islanding" that is pervasive when two or more chemically distinct adsorbates are used to form mixed SAMs. Such homogeneously mixed films offer the opportunity to fine-tune the interfacial properties of a substrate and to create unique heterogeneous interfaces that are well defined by the chemical composition of the tailgroups exposed at the surface. The insight derived from these studies opens the door to new uses for SAMs, both in surface engineering applications (such as corrosion resistance and soft lithographic patterning) and in the stabilization and manipulation of nanoparticles.
Self-assembled monolayers (SAMs) on gold derived from the direct adsorption of thioacetic acid S-decyl ester (C10SAc) and thioacetic acid S-octadecyl ester (C18SAc) were compared to the corresponding SAMs derived from the analogous adsorption n-decanethiol (C10SH) and n-octadecanethiol (C18SH). All SAMs were characterized using ellipsometry, contact angle goniometry, polarization modulation infrared reflection absorption spectroscopy (PM-IRRAS), and X-ray photoelectron spectroscopy (XPS). The comparison revealed that the SAMs generated from the thioacetates are not as densely packed and well ordered as the SAMs generated from the thiols. Furthermore, studies of the kinetics of adsorption found that the thioacetates adsorb more slowly than the corresponding thiols.
The interfacial electrochemical properties of self-assembled monolayers (SAMs) on gold derived from a structurally tailored series of monodentate, bidentate, and tridentate chelating alkanethiols were investigated. Specific adsorbates included 1-hexadecanethiol (C16), 2-tetradecylpropane-1,3-dithiol (C16C2), 2-tetradecyl-2-methylpropane-1,3-dithiol (C16C3), 2,2-ditetradecylpropane-1,3-dithiol (C16C16), and 1,1,1-tris(mercaptomethyl)pentadecane (t-C16). Reductive desorption of the SAMs as a function of potential was probed by voltammetric measurements, which indicated the following relative order of electric potential stability: t-C16 > C16C2 ≈ C16C3 ≈ C16C16 > C16. The ionic permeability was investigated under various applied cathodic potentials by electrochemical impedance spectroscopy (EIS). An examination of SAMs prepared at room temperature and accessed by EIS at open-circuit potential showed that the ionic permeability increased in the order C16C2 < C16 < C16C3 < C16C16 < t-C16. The ionic permeability of films was further influenced by the electric potential of the metal substrate and the temperature at which the monolayers were assembled. The potential dependence of the ionic permeability was qualitatively rationalized by considering both the initial ionic permeability and the electric potential stability of the SAMs. Similarly, the ionic permeability of the SAMs prepared at elevated temperature showed contributions from both their thermal stability and their insulating properties at room temperature.
Self-assembled monolayers (SAMs) were prepared on gold substrates from an unsymmetrical partially fluorinated spiroalkanedithiol adsorbate with the specific structure of [CH3(CH2)7][CF3(CF2)7(CH2)8]C[CH2SH]2 (SADT) and compared to SAMs formed from the semifluorinated monothiol F8H10SH [CF3(CF2)7(CH2)10SH] of analogous chain length and n-octadecanethiol. The adsorbate with two alkyl chains, one terminally fluorinated and the other nonfluorinated, was designed to form monolayers in which the bulky helical fluorocarbon segments assemble on top of an underlying layer of well-packed trans-extended alkyl chains. Different combinations of deposition solvents and temperatures were used to produce the bidentate SAMs. Characterization of the resulting monolayers revealed that SAMs formed in DMF at room temperature allow complete binding of the sulfur headgroups to the surface and exhibit higher conformational order than those produced using alternative solvent/temperature combinations. The reduced film thicknesses and enhanced wettability of the SADT SAMs, as compared to the SAMs generated from F8H10SH, suggest loose packing and an increase in the tilt of the terminal fluorocarbon chain segments. Nevertheless, the density of the underlying hydrocarbon chains of the SADT SAMs was higher than that of the F8H10SH SAMs, owing to the double-chained structure of the new adsorbate. The conformational orders of the SAM systems were observed to decrease as follows: C18SH > F8H10SH > SADT. However, the SAMs formed from this new double-chained bidentate adsorbate in DMF expose a fluorinated interface with a relatively low surface roughness, as determined by contact-angle hysteresis.
Organic thin-films on gold were prepared from a set of new, custom-designed bidentate alkanethiols possessing a mixture of normal alkane and methoxy-terminated tri(ethylene glycol) chains. The new unsymmetrical spiroalkanedithiol adsorbates were of the form [CHO(CHCHO)(CH)]-[CH(CH)]C[CHSH] where n = 3 and 14; designated EG3C7-C7 and EG3C7-C18, respectively. Their corresponding self-assembled monolayers (SAMs) on gold were characterized and compared with monothiol SAMs derived from an analogous normal alkanethiol (C18SH) and an alkanethiol terminated with an oligo(ethylene glycol) (OEG) moiety (i.e., EG3C7SH). Ellipsometric data revealed reduced film thicknesses for the double-chained dithiolate SAMs, which perhaps arose from the phase-incompatible merger of a hydrocarbon chain with an OEG moiety, contributing to disorder in the films and/or an increase in chain tilt. The comparable wettabilities of the SAMs derived from EG3C7SH and EG3C7-C7, using water as the contacting liquid, are consistent with exposure of the OEG moieties at both interfaces, whereas the lower wettability of the SAM derived from EG3C7-C18 is consistent with exposure of hydrocarbon chains at the interface. The data collected by X-ray photoelectron spectroscopy confirmed the formation of the new OEG-terminated dithiolate SAMs, and also revealed them as less densely packed monolayers due in part to the large molecular cross section of the OEG moieties and to their double-chained structure with dual surface bonds. Mixed SAMs formed from pairs of monothiols having chain compositions analogous to those of the chains of the new dithiols showed that an EG3C7SH/heptanethiol-mixed SAM and the EG3C7-C7 SAM produced almost identical characterization data, revealing the favorable film formation dynamics for adsorbate structures where the alkyl chains can assemble beneath the phase-incompatible OEG termini. For the mixed SAM formed from EG3C7SH/C18SH, the data indicate that the EG3C7SH component failed to incorporate in the film, demonstrating that the blending of phase-incompatible chains is sometimes best accomplished when both chains exist on a single adsorbate structure. Furthermore, the results of solution-phase thermal desorption tests revealed that the OEG-terminated films generated from the bidentate EG3C7-C7 and EG3C7-C18 adsorbates exhibit enhanced thermal stability when compared to the film generated from monodentate EG3C7SH. In a brief study of protein adsorption, the multicomponent SAMs showed a greater ability to resist the adsorption of fibrinogen on their surfaces when compared to the SAM derived from C18SH, but not better than the monolayer derived from EG3C7SH.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.